Oxidation behaviour of a MoSi2-based composite in different atmospheres in the low temperature range (400–550 °C)
-
- Hansson, Kristina, 1971 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Halvarsson, Mats, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Tang, Jun Eu, 1974 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
Pompe, Robert (författare)
-
Sundberg, Mats, 1964 (författare)
-
- Svensson, Jan-Erik, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2004
- 2004
- Engelska.
-
Ingår i: Journal of the European Ceramic Society. - : Elsevier BV. - 1873-619X .- 0955-2219. ; 24:13, s. 3559-3573
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The oxidation characteristics of a MoSi2-based composite within the temperature range of 400–550 °C were investigated. The effects of temperature and water vapour on oxidation were examined. The oxidation kinetics were studied using a thermobalance, while the morphology and composition of the oxides were examined using XRD, ESEM/EDX, and SEM/EDX.The peak oxidation rates in dry O2 and View the MathML source were found to occur at temperatures of approximately 510 and 470 °C, respectively. Within the temperature range of accelerated oxidation (400–500 °C), the oxidation rate in View the MathML source was substantially higher than that in dry O2. At higher temperatures, the oxidation rate decreased, and the magnitude of the decrease was steeper and occurred at a lower temperature for View the MathML source (510 °C) than for O2 (550 °C). Furthermore, the rate of depletion of molybdenum (Mo) from the oxide scales during oxidation increased with increasing temperature and water vapour content. It appears that Mo loss is a key process influencing the protective properties of the oxide layer on the MoSi2 composite. A potential mechanism for the different oxidation behaviours in O2 and View the MathML source is proposed.
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Nyckelord
- SiO2
- Refractories
- Silicides
- MoSi2
- Oxidation
- Corrosion
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas