Simultaneous Strength-Ductility Enhancement of a Nano-Lamellar AlCoCrFeNi2.1 Eutectic High Entropy Alloy by Cryo-Rolling and Annealing
-
- Bhattacharjee, T. (författare)
- Kyoto University
-
- Wani, I. S. (författare)
- Indian Institute of Technology Hyderabad
-
- Sheikh, Saad Ahmed, 1987 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
Clark, I. T. (författare)
-
Okawa, T. (författare)
-
- Guo, Sheng, 1981 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Bhattacharjee, P. P. (författare)
- Indian Institute of Technology Hyderabad
-
- Tsuji, N. (författare)
- Kyoto University
-
visa färre...
-
(creator_code:org_t)
- 2018-02-19
- 2018
- Engelska.
-
Ingår i: Scientific Reports. - : Springer Science and Business Media LLC. - 2045-2322 .- 2045-2322. ; 8:1
- Relaterad länk:
-
https://research.cha... (primary) (free)
-
visa fler...
-
https://www.nature.c...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- Nano-lamellar (L1 2 + B2) AlCoCrFeNi 2.1 eutectic high entropy alloy (EHEA) was processed by cryo-rolling and annealing. The EHEA developed a novel hierarchical microstructure featured by fine lamellar regions consisting of FCC lamellae filled with ultrafine FCC grains (average size ∼200-250 nm) and B2 lamellae, and coarse non-lamellar regions consisting of ultrafine FCC (average size ∼200-250 nm), few coarse recrystallized FCC grains and rather coarse unrecrystallized B2 phase (∼2.5 μm). This complex and hierarchical microstructure originated from differences in strain-partitioning amongst the constituent phases, affecting the driving force for recrystallization. The hierarchical microstructure of the cryo-rolled and annealed material resulted in simultaneous enhancement in strength (Yield Strength/YS: 1437 ± 26 MPa, Ultimate Tensile Strength/UTS: 1562 ± 33 MPa) and ductility (elongation to failure/e f ∼ 14 ± 1%) as compared to the as-cast as well as cold-rolled and annealed materials. The present study for the first time demonstrated that cryo-deformation and annealing could be a novel microstructural design strategy for overcoming strength-ductility trade off in multiphase high entropy alloys.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas