Nano-cellulosic materials: The impact of water on their dissolution in DMAc/LiCl
-
- Hasani, Merima, 1978 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
Henniges, U. (författare)
-
- Idström, Alexander, 1983 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Nordstierna, Lars, 1976 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Westman, Gunnar, 1964 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
Rosenau, T. (författare)
-
Potthast, A. (författare)
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2013
- 2013
- Engelska.
-
Ingår i: Carbohydrate Polymers. - : Elsevier BV. - 0144-8617. ; 98:2, s. 1565-1572
- Relaterad länk:
-
https://research.cha...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The dissolution behaviour of disassociated cellulosic materials in N,N-dimethylacetamide/lithium chloride (DMAc/LiCl) was investigated. The parameters monitored were chromatographic elution profiles and recovered mass by means of gel permeation chromatography (GPC) with RI detection. In order to elucidate the impact of the disassembly on cellulosic fibres, comparative studies were performed with the non-disassociated cellulose counterparts. The importance of the presence of water was addressed by Karl Fischer titration and solvent exchange experiments. Morphological changes during the dissolution process were studied by scanning electron microscopy (SEM). Dissolution of fibrillated cellulosic materials is impeded compared to the non-fibrillated material. This is a consequence of the high-surface-area fibrils prone to retain high amounts of water. Dissolution behaviour of nano-crystalline cellulosic materials appeared to be source-dependent. Due to the absence of entangled networks, these materials retain only water bound at the surface of the nano-crystallites, indicative of both the exposed surface area and solubility. The small cellulose nano-particles extracted from dissolving pulp show lower solubility compared to the large NCC particles from cotton.
Ämnesord
- NATURVETENSKAP -- Kemi -- Fysikalisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Physical Chemistry (hsv//eng)
Nyckelord
- Gel permeation chromatography
- Fibrillated cellulose
- Water content
- Dissolution kinetics
- Fibre morphology
- Accessibility