Effect of cooling rate and Ti addition on the microstructure and mechanical properties in as-cast condition of hypereutectic high chromium cast irons
-
- Liu, Qiang (author)
- KTH,Tillämpad processmetallurgi
-
Zhang, Hongwei (author)
-
Wang, Qiang (author)
-
show more...
-
Zhou, Xiangkui (author)
-
- Jönsson, Pär G. (author)
- KTH,Tillämpad processmetallurgi
-
- Nakajima, Keiji (author)
- KTH,Tillämpad processmetallurgi
-
show less...
-
(creator_code:org_t)
- Iron and Steel Institute of Japan, 2012
- 2012
- English.
-
In: ISIJ International. - : Iron and Steel Institute of Japan. - 0915-1559 .- 1347-5460. ; 52:12, s. 2210-2219
- Related links:
-
https://www.jstage.j...
-
show more...
-
https://urn.kb.se/re...
-
https://doi.org/10.2...
-
show less...
Abstract
Subject headings
Close
- The effect of cooling rate and Ti additions on the mechanical properties and carbides characteristics such as morphology, size distribution and composition was studied in high-chromium cast irons containing Fe-17 mass%Cr-4 mass%C. Based on the size distribution, composition and morphology, M 7C3 type carbides were roughly classified into "primary M7C3 carbides" and "eutectic M7C3 carbides" with a 11.2μ m border size. Thereafter, the change of the solidification structure and especially the refinement of carbides size were determined. It was found that both the size and number values should be summarized systematically for primary M 7C3 carbides and eutectic M7C3 carbides, respectively. Also, TiC carbides with a high formation temperature can not only act as a nuclei of M7C3 carbides, but they also contain a Ti(C, N) core. In the as-cast condition, the bulk hardness of the cast irons increases with an increased Ti content. In addition, the wear loss increases with an increased Ti content. Neither the bulk hardness nor the wear loss did change too much with an increased cooling rate.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Keyword
- Carbides size distributions
- Cooling rate
- High chromium cast irons
- M7C3
- Ti addition
- TiC