Single-step electrodeposition of polycrystalline CdSe microwire arrays : structural and optical properties
-
Riveros, G (författare)
-
Vasques, J (författare)
-
Gomes, H (författare)
-
visa fler...
-
- Makarova, Tatiana (författare)
- Umeå universitet,Institutionen för fysik
-
Silva, D (författare)
-
Marotti, R (författare)
-
Dalchiele, E (författare)
-
visa färre...
-
(creator_code:org_t)
- 2007-11-13
- 2008
- Engelska.
-
Ingår i: APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING. - : Springer Berlin/Heidelberg. - 0947-8396. ; 90:3, s. 423-430
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- In this work we report on the single-step synthesis of CdSe microwires with good crystalline characteristics by template-assisted electrochemical deposition from an electrolytic solution containing CdSO4Ce+CeSeO2 and sulfuric acid. Deposition was conducted at three different temperatures (25 degrees C, 60 degrees C and 80 degrees C) under potentiostatic control using a commercial nanoporous alumina membrane as the working electrode. The best results were obtained when the electrodeposition was carried out at E=-0.610 V vs. Ag/AgCl and T=80 degrees C. Under these experimental conditions, the microwires are uniform, well aligned, have a high packing density, and present a good crystalline character according to XRD analysis. TEM observations revealed that they are dense and continuous, with a mean diameter ranging from 360-380 nm, greater than the channel diameters of the alumina template used. A detailed study of the reflectance in the region close to CdSe bandgap energy allows the determination of a weak direct absorption edge at 1.65 eV, close to the bulk bandgap energy. The Raman spectra consist of a strong mode centered at 208 cm(-1) arising from the LO phonon and a somewhat weak, but still strong, mode arising from the second order LO (2LO) appearing at 415 cm(-1)
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas