In situ polymerization of polyaniline in wood veneers

• The present study describes the possibility to polymerize aniline within wood veneers to obtain a semi-conducting material with solid wood acting as the base template. It was determined that it is possible to synthesize the intrinsically conductive polymer (ICP) polyaniline in situ within the wood structure of Southern yellow pine veneers, combining the strength of the natural wood structure with the conductivity of the impregnated polymer. It was found that polyaniline is uniformly dispersed within the wood structure by light microscopy and FT-IR imaging. A weight percent gain in the range of 3−12 wt % was obtained with a preferential formation in the wood structure and cell wall, rather than in the lumen. The modified wood was found to be less hydrophilic with the addition of phosphate doped polyaniline as observed by equilibrium water swelling studies. While wood itself is insulating, the modified veneers had conductivities of 1 × 10−4 to 1 × 10−9 S cm−1, demonstrating the ability to tune the conductivity and allowing for materials with a wide range of applications, from anti-static to charge-dispersing materials. Furthermore, the modified veneers had lower total and peak heat releases, as determined by cone calorimetry, because of the char properties of the ICP. This is of interest if these materials are to be used in building and furniture applications where flame retardance is of importance.

Ämnesord

LANTBRUKSVETENSKAPER  -- Lantbruksvetenskap, skogsbruk och fiske (hsv//swe)

AGRICULTURAL SCIENCES  -- Agriculture, Forestry and Fisheries (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

Nyckelord

Aniline

Conducting polymers

Infrared imaging

Refining

Swelling

Veneers

Wooden buildings

Conducting materials

Cone calorimetry

Doped polyaniline

Flame-retardance

In-situ polymerization

Intrinsically conductive polymers

Southern yellow pines

Weight percent

Wood

Publikations- och innehållstyp

ref (ämneskategori)

kon (ämneskategori)