SwePub
Sök i SwePub databas

  Utökad sökning

Träfflista för sökning "WFRF:(Liu A H) srt2:(1990-1994)"

Sökning: WFRF:(Liu A H) > (1990-1994)

  • Resultat 1-4 av 4
Sortera/gruppera träfflistan
   
NumreringReferensOmslagsbildHitta
1.
  • Szymanski, J. J., et al. (författare)
  • MEGA : A search for the decay mu –> e gamma
  • 1994
  • Ingår i: Intersections between particle and nuclear physics. Proceedings, 5th Conference, St. Petersburg, USA, May 31-June 6, 1994. ; , s. 789-792
  • Konferensbidrag (refereegranskat)
  •  
2.
  •  
3.
  • Amann, F., et al. (författare)
  • A search for murarregamma at the level of 10-13
  • 1991
  • Ingår i: Proceedings of the 25th International Conference on High Energy Physics. - 9810024347 ; , s. 1070-1071
  • Konferensbidrag (refereegranskat)abstract
    • The MEGA experiment, which is a search for the decay murarregamma with a branching ratio sensitivity of about 10-13, employs highly modular, fast detectors, state-of-the-art electronics, and a staged trigger with on-line filters. The detectors are contained in a 1.5-T solenoidal field produced by a superconducting magnet. Positrons are confined to the central region and are measured by a set of thin MWPCs. Photons are measured by one of four layers of pair spectrometers in the outer region. Most aspects of the design have been validated in engineering runs; data taking will begin in 1990 with much of the electron arm and one pair spectrometer layer installed.
  •  
4.
  • Dou, S.X., et al. (författare)
  • Improvement of critical current density in the Bi-Pb-Sr-Ca-Cu-O system through hot isostatic pressing
  • 1990
  • Ingår i: Physica. C, Superconductivity. - 0921-4534 .- 1873-2143. ; 167:5-6, s. 525-528
  • Tidskriftsartikel (refereegranskat)abstract
    • The effects of hot isostatic pressing (HIPing) on densification and the superconducting properties of the Bi-Pb-Sr-Ca-O system were investigated. A relative density up to 95% and a critical current density greater than 1100 A/cm2 at 77 K were achieved through HIPing at 650°C for 2 h under 200 MPa argon. Under these conditions, the product gave a value of Jc four times that without HIPing. To was unaffected by HIPing for samples encapsulated with a combination of glass and silver tubes. However, To was suppressed from 103 K to 86 K for samples encapsulated with stainless steel and silver tubes while Jc increased from 260 A/ cm2 to 1086 A/cm2 during HIPing, indicating that the weak links were significantly improved. A new minor phase, having a composition of Bi/Pb/Sr/Ca/Cu=0.58/2.8/3.0/2.1/1.1, was observed in HIPed samples but its effect on Jc is not clear
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-4 av 4

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy