- Carabante, Ivan, et al.
(författare)
-
Adsorption of As (V) on iron oxide nanoparticle films studied by in situ ATR-FTIR spectroscopy
- 2009
-
Ingår i: Colloids and Surfaces A. - : Elsevier BV. - 0927-7757 .- 1873-4359. ; 346:1-3, s. 106-113
-
Tidskriftsartikel (refereegranskat)abstract
- Stabilization of arsenic contaminated soils by iron oxides has been proposed as a remediation technique to prevent leaching of arsenate into the environment. Fundamental studies are needed to establish under which conditions the complexes formed are stable. In the present work, a powerful technique, viz. ATR-FTIR spectroscopy, is adapted to studies of adsorption of arsenate species on iron oxides. This technique facilitates acquisition of both quantitative and qualitative in situ adsorption data.In the present work, about 800 nm thick films of 6-lineferrihydrite were deposited on ZnSe ATR crystals. Arsenate adsorption on the ferrihydrite film was studied at pD values ranging from 4 to 12 and at an arsenate concentration of 0.03 mM in D2O solution. The amount of adsorbed arsenate decreased with increasing pD as a result of the more negatively charged iron oxide surface at higher pD values. The adsorption and desorption kinetics were also studied. Arsenate showed a higher adsorption rate within the first 70 minutes and a much lower adsorption rate from 70 up to 300 minutes. The low adsorption rate at longer reaction times was partly due to a low desorption rate of already adsorbed carbonate species adsorbed at the surface. The desorption of carbonate species was evidenced by the appearance of negative absorption bands. The desorption of adsorbed arsenate complexes was examined by flushing with D2O at pD 4 and 8.5 and it was found that the complexes were very stable at pD 4 suggesting formation of mostly inner-sphere complexes whereas a fraction of the complexes at pD 8.5 were less stable than at pD 4, possibly due to the formation of outer-sphere complexes.In summary, the ATR technique was shown to provide in situ information about the adsorption rate, desorption rate and the speciation of the complexes formed within a single experiment, which is very difficult to obtain using other techniques.
|
|
| 3. |
- Carabante, Ivan
(författare)
-
Study of arsenate adsorption on iron oxide by in situ ATR-FTIR spectroscopy
- 2009
-
Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Stabilization of arsenic contaminated soils by iron oxides has been proposed as a remediation technique to prevent leaching of arsenate into the environment. However, fundamental studies are needed to establish under which conditions the complexes formed are stable. A new method based on ATR-FTIR spectroscopy was adapted to study the adsorption of arsenate species on iron oxides. The measurements required the use of D2O as solvent. The amount of arsenate complexes adsorbed on the iron oxide increased with decreasing pD in the range studied, viz. pD 4-12. Arsenate complexes adsorbed at pD 4 desorbed from the film to some extent as the pD was increased to 8.5 or 12. The stability of arsenate complexes adsorbed on the iron oxide evidently changed with the change in pD, most likely due to the electrostatic repulsion between the negatively charged oxoanion and the more negatively charged iron oxide as the pD increased. From competitive adsorption experiments it was found that arsenate species were more strongly bonded to the iron oxide than phosphate species. Furthermore, it was found that two different phosphate complexes formed on the iron surface at pD 4, one deuterated and the other one de-deuterated. The complexes showed very different stability. The deuterated phosphate complex was desorbed easily from the iron oxide film as arsenate was added to the system whereas the de-deuterated phosphate complex only desorbed slightly from the film upon adding arsenate.This work has increased the fundamental knowledge of the iron oxide/arsenate/phosphate system, which will be of importance for the development of more effective soil remediation techniques.
|
|