- Cervin, Nicholas Tchang, et al.
(författare)
-
Strong, Water-Durable, and Wet-Resilient Cellulose Nanofibril-Stabilized Foams from Oven Drying
- 2016
-
Ingår i: ACS Applied Materials and Interfaces. - : American Chemical Society (ACS). - 1944-8244 .- 1944-8252. ; 8:18, s. 11682-11689
-
Tidskriftsartikel (refereegranskat)abstract
- Porous materials from cellulose nanofibrils (CNFs) have been prepared using Pickering foams from aqueous dispersions. Stable wet foams were first produced using surface-modified CNFs as stabilizing particles. To better maintain the homogeneous pore structure of the foam after drying, the foams were dried in an oven on a liquid-filled porous ceramic frit. The cell structure was studied by scanning electron microscopy and liquid porosimetry, the mechanical properties were studied by compression testing, and the liquid absorption capacity was determined both with liquid porosimetry and by soaking in water. By controlling the charge density of the CNFs, it was possible to prepare dry foams with different densities, the lowest density being 6 kg m(-3), that is, a porosity of 99.6%. For a foam with a density of 200 kg m(-3) the compressive Young's modulus was 50 MPa and the energy absorption to 70% strain was 2.3 MJ M-3. The use of chemically modified CNFs made it possible to prepare cross-linked foams with water-durable and wet-resilient properties. These foams absorbed liquid up to 34 times their own weight and were able to release this liquid under compression and to reabsorb the same amount when the pressure was released.
|
|
| 2. |
- Mushi, Ngesa Ezekiel Zekiel, et al.
(författare)
-
Nanostructurally Controlled Hydrogel Based on Small-Diameter Native Chitin Nanofibers : Preparation, Structure, and Properties
- 2016
-
Ingår i: ChemSusChem. - : Wiley-VCH Verlagsgesellschaft. - 1864-5631 .- 1864-564X.
-
Tidskriftsartikel (refereegranskat)abstract
- Chitin nanofibers of unique structure and properties can be obtained from crustacean and fishery waste. These chitin nanofibers have roughly 4nm diameters, aspect ratios between 25-250, a high degree of acetylation and preserved crystallinity, and can be potentially applied in hydrogels. Hydrogels with a chitin nanofiber content of 0.4, 0.6, 0.8, 1.0, 2.0, and 3.0wt% were successfully prepared. The methodology for preparation is new, environmentally friendly, and simple as gelation is induced by neutralization of the charged colloidal mixture, inducing precipitation and secondary bond interaction between nanofibers. Pore structure and pore size distributions of corresponding aerogels are characterized using auto-porosimetry, revealing a substantial fraction of nanoscale pores. To the best of our knowledge, the values for storage (13kPa at 3wt%) and compression modulus (309kPa at 2wt%) are the highest reported for chitin nanofibers hydrogels.
|
|