Gelatin-fibrinogen cryogel dermal matrices for wound repair: Preparation, optimisation and in vitro study.
-
Dainiak, Maria B (författare)
-
Allan, Iain U (författare)
-
Savina, Irina N (författare)
-
visa fler...
-
Cornelio, Lisa (författare)
-
James, Elizabeth S (författare)
-
James, Stuart L (författare)
-
Mikhalovsky, Sergey V (författare)
-
Jungvid, Hans (författare)
-
- Galaev, Igor (författare)
- Lund University,Lunds universitet,Bioteknik,Centrum för tillämpade biovetenskaper,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Biotechnology,Center for Applied Life Sciences,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2010
- 2010
- Engelska.
-
Ingår i: Biomaterials. - : Elsevier BV. - 1878-5905 .- 0142-9612. ; 31, s. 67-76
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Macroporous sponge-like gelatin-fibrinogen (Gl-Fg) scaffolds cross-linked with different concentrations (0.05-0.5%) of glutaraldehyde (GA) were produced using cryogelation technology, which allows for the preparation of highly porous scaffolds without compromising their mechanical properties, and is a more cost-efficient process than freeze-drying. The produced Gl-Fg-GA(X) scaffolds had a uniform interconnected open porous structure with a porosity of up to 90-92% and a pore size distribution of 10-120mum. All of the obtained cryogels were elastic and mechanically stable, except for the Gl-Fg-GA(0.05) scaffolds. Swelling kinetics and degradation rate, but not the porous structure of the cryogels, were strongly dependent on the degree of cross-linking. A ten-fold increase in the degree of cross-linking resulted in an almost 80-fold decrease in the rate of degradation in a solution of protease. Cryogels were seeded with primary dermal fibroblasts and the densities observed on the surface, plus the expression levels of collagen types I and III observed 5 days post-seeding, were similar to those observed on a control dermal substitute material, Integra((R)). Fibroblast proliferation and migration within the scaffolds were relative to the GA content. Glucose consumption rate was 3-fold higher on Gl-Fg-GA(0.1) than on Gl-Fg-GA(0.5) cryogels 10 days post-seeding. An enhanced cell motility on cryogels with reducing GA crosslinking was obtained after long time culture. Particularly marked cell infiltration was seen in gels using 0.1% GA as a crosslinker. The scaffold started to disintegrate after 42 days of in vitro culturing. The described in vitro studies demonstrated good potential of Gl-Fg-GA(0.1) scaffolds as matrices for wound healing.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Industriell bioteknik -- Bioteknisk apparatteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Industrial Biotechnology -- Bioengineering Equipment (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas