| 1. |
- Kall, M., et al.
(författare)
-
Resonance Raman scattering as a probe of oxygen dynamics in YBa2Cu3Ox
- 1998
-
Ingår i: Journal of Physics and Chemistry of Solids. - 0022-3697 .- 1879-2553. ; 59, s. 1988-1990
-
Tidskriftsartikel (refereegranskat)abstract
- We report on the metastable photo-bleaching of the 2.15 eV yellow Raman resonance in oxygen deficient YBa2Cu3Ox (x = 6.35-6.87), extending investigations by Wake ct al. (Phys. Rev. Lett., 1991,67, 3728) for x approximate to 7. Polarization, x dependence and phonon spectra indicate that the resonance is localized at oxygen vacancies in long CuO-chains. The resonance is thermally reactivated from the metastable bleached state with a relaxation time tau similar to exp[Delta/k(B)T] with Delta approximate to 1 eV. The resulting temperature dependent equilibrium resonance intensity essentially miners the oxygen superstructure disordering around T* approximate to 100 degrees C observed in the same crystals by hard X-ray diffraction, thus offering a new effective probe of chain-oxygen dynamics in YBa2Cu3Ox. (C) 1998 Elsevier Science Ltd. All rights reserved.
|
|
| 2. |
- Kakihana, M., et al.
(författare)
-
A simple and reproducible way to synthesize PrBa2Cu4O8 under 1 atm of oxygen by amorphous citrate method
- 1999
-
Ingår i: Physica. C, Superconductivity. - 0921-4534 .- 1873-2143. ; 321, s. 74-80
-
Tidskriftsartikel (refereegranskat)abstract
- A simple aqueous solution technique utilizing citric acid (CA) as a complexant was applied to prepare PrBa2Cu4O8 (Pr124) at ambient oxygen pressure. Heating of a mixed-solution of CA, water (H2O) and ions of Pr, Ba and Cu with a molar ratio of [CA]:[H2O]:[Pr + Ba + Cu] = 3.6:40:1 on a hot-plate set at 200 degrees C produced a transparent amorphous citrate "gel" without any precipitation, which after heat-treatment at 450 degrees C was converted to a precursor for Pr124. The Pr124 compound with only minor traces of BaCuO2, PrBaO3 and CuO formed after heat-treating the precursor twice at 850 degrees C for 60 h under 1 atm oxygen pressure. The amount of impurities in the citrate-derived Pr124 was approximately half of that in the best sample previously prepared by the more elaborate high-pressure technique. (C) 1999 Elsevier Science B.V. All rights reserved.
|
|