Surface pore initiated fatigue failure in laser clad components

• A laser clad and machined cylindrical structural steel rod was fatigue tested under four-point bending load. The resulting fracture could be tracked back to a spherical surface pore in the Co-based coating. Due to an oxide inclusion, the pore was not identified by dye penetrant inspection. Two circular buckling strain patterns that were detected beside the pore at the surfaces after fracture confirm local plastic deformation prior to crack initiation. In order to calculate the stress field around the surface pore, linear elastic finite element analysis was carried out. For four-point bending load, a surface pore generally exceeds the maximum stress of a smooth rod as long as the pore is located within an azimuthal angle of ±55°, which was the case for the presented as well as for another pore initiated sample.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

Nyckelord

Produktionsutveckling

Manufacturing Systems Engineering

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)