| 1. |
- Klechikov, Alexey, et al.
(författare)
-
Multilayered intercalation of 1-octanol into Brodie graphite oxide
- 2017
-
Ingår i: Nanoscale. - : Royal Society of Chemistry (RSC). - 2040-3364 .- 2040-3372. ; 9:20, s. 6929-6936
-
Tidskriftsartikel (refereegranskat)abstract
- Multilayered intercalation of 1-octanol into the structure of Brodie graphite oxide (B-GO) was studied as a function of temperature and pressure. Reversible phase transition with the addition/removal of one layer of 1-octanol was found at 265 K by means of X-ray Diffraction (XRD) and Differential Scanning Calorimetry (DSC). The same transition was observed at ambient temperature upon a pressure increase above 0.6 GPa. This transition was interpreted as an incongruent melting of the low temperature/high pressure B-GO intercalated structure with five layers of 1-octanol parallel to GO sheets (L-solvate), resulting in the formation of a four-layered structure that is stable under ambient conditions (A-solvate). Vacuum heating allows the removal of 1-octanol from the A-solvate layer by layer, while distinct sets of (00 l) reflections are observed for three-, two-, and one-layered solvate phases. Step by step removal of the 1-octanol layers results in changes of distance between graphene oxide planes by similar to 4.5 angstrom. This experiment proved that both L- and A-solvates are structures with layers of 1-octanol parallel to GO planes. Unusual intercalation with up to five distinct layers of 1-octanol is remarkably different from the behaviour of small alcohol molecules (methanol and ethanol), which intercalate B-GO structure with only one layer under ambient conditions and a maximum of two layers at lower temperatures or higher pressures. The data presented in this study make it possible to rule out a change in the orientation of alcohol molecules from parallel to perpendicular to the GO planes, as suggested in the 1960s to explain larger expansion of the GO lattice due to swelling with larger alcohols.
|
|
| 2. |
- Sun, Jinhua, et al.
(författare)
-
Porous graphite oxide pillared with tetrapod-shaped molecules
- 2017
-
Ingår i: Carbon. - : Elsevier. - 0008-6223 .- 1873-3891. ; 120, s. 145-156
-
Tidskriftsartikel (refereegranskat)abstract
- Porous pillared graphene oxide (GO) materials were prepared using solvothermal reaction of Hummers GO with solution of Tetrakis(4-aminophenyl)methane (TKAm) in methanol. The intercalation of TKAm molecules between individual GO sheets, performed under swelling condition, results in expansion of inter-layer distance of GO from ∼7.5 Å to 13-14 Å. Pillaring GO with bulky, rigid 3D shaped TKAm molecules could be an advantage for the preparation of stable pillared structures compared to e.g. aliphatic or aromatic diamines. Insertion of TKAm molecules into inter-layer space of GO results in formation of interconnected network of sub-nanometer slit pores. The expanded GO structure prepared with optimized GO/TKAm composition shows Specific Surface Area (SSA) up to 660 m2/g which is among the highest reported for GO materials pillared using organic spacers. Modelling of GO structures pillared with TKAm molecules shows that maximal SSA of about 2300 m2/g is theoretically possible for realistic concentration of pillaring molecules in GO interlayers. Hydrogen sorption by pillared GO/TKAm is found to follow standard correlation with SSA both at ambient and liquid nitrogen temperatures with highest uptakes of 1.66 wt% achieved at 77 K and 0.25 wt% at 295 K. Our theoretical simulations show that pillared GO structures do not provide improvement of hydrogen storage beyond well-established physisorption trends even for idealized materials with subnanometer pores and SSA of 2300–3700 m2/g.
|
|