Zirconia-Supported Vanadium Oxide Catalysts for Ammoxidation and Oxidation of Toluene: A Characterization and Activity Study
-
- Sanati, Mehri (författare)
- Lund University,Lunds universitet,Ergonomi och aerosolteknologi,Institutionen för designvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Ergonomics and Aerosol Technology,Department of Design Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Andersson, Arne (författare)
- Lund University,Lunds universitet,Avdelningen för kemiteknik,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Division of Chemical Engineering,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
Wallenberg, L R (författare)
-
visa fler...
-
Rebenstorf, B (författare)
-
visa färre...
-
(creator_code:org_t)
- 1993
- 1993
- Engelska.
-
Ingår i: Applied Catalysis A: General. - 0926-860X. ; 106:1, s. 51-72
- Relaterad länk:
-
http://dx.doi.org/10... (free)
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- A series of samples of vanadia supported on monoclinic zirconia were prepared with nominal loadings from a half up to sixteen theoretical vanadia layers. The samples were characterized with X-ray diffraction, scanning electron microscopy combined with energy dispersive X-ray analysis, high-resolution electron microscopy, Raman and diffuse reflectance infrared spectroscopy, and were used in the oxidation and the ammoxidation of toluene. At loadings in the monolayer range, Raman and infrared bands from decavanadate-like and dehydrated tetrahedral vanadia species were at ca. 990 and ca. 1025 cm−1, respectively. Raman bands at 821 and 880 cm−1 were present only at the lowest loading and are characteristic of orthovanadate and pyrovanadate species, respectively. X-ray diffraction, Raman and infrared spectroscopic results revealed formation of some crystalline V2O5 and ZrV2O7 at loadings exceeding a theoretical monolayer. In this case, consideration of Raman intensity variations allowed the conclusion that additional non-crystalline vanadia must be present. According to high-resolution electron micrographs, this vanadia consists of an amorphous overlayer, 4–8 atomic layers thick. In toluene oxidation zirconia-supported vanadia compared with crystalline V2O5 was found less selective for benzaldehyde formation. In toluene ammoxidation, on the other hand, vanadia on zirconia was found to possess good activity and selectivity for benzonitrile formation. Amorphous vanadia was the most active structure on zirconia, while the selectivities for nitrile and aldehyde formations were almost independent of the loading for one theoretical layer and above.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Produktionsteknik, arbetsvetenskap och ergonomi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Production Engineering, Human Work Science and Ergonomics (hsv//eng)
Nyckelord
- catalyst characterization (BET/XRD/DRIFTS/FT-Raman spectroscopy/EDX/SEM / HREM)
- toluene oxidation
- toluene ammoxidation
- vanadie-zirconia
- zirconia (monoclinic)