  • Birch, J., et al. (författare)
  • Growth and structural characterization of single-crystal (001) oriented Mo V superlattices
  • 1990
  • Ingår i: Vacuum. - 0042-207X. ; 41:4-6, s. 1231-1233
  • Tidskriftsartikel (refereegranskat)abstract
    • Dual target magnetron sputtering has been used to grow single-crysal MoV superlattice structures (SLS) with modulation wavelengths λ ranging from 0.6 to 17.7 nm on (001) oriented MgO substrates held at temperatures Ts between 600 and 900°C. High resolution cross-sectional transmission electron microscopy (HRXTEM) images and comparisions between experimental and calculated X-ray diffraction (XRD) spectra show that SLS with an interface sharpness of ±1 monolayer (±0.15 nm) could be grown for λ ⩽ 4.9 nm and Ts ⩽ 700°C whereas interdiffusion broadened the interfaces for higher Ts values. This interface sharpness was also verified by growing SLS with λ = 0.6 nm (one unit cell of Mo and one of V) which exhibited strong superlattice satellites in both XRD and selected area electron diffraction (SAED), and contrast from the individual layers was also observed in HRXTEM images. For λ > 4.9 nm, HRXTEM images showed non-uniform layers and the XRD peak width (FWHM) increased by 250%.
  •  
3.
  • Birch, J., et al. (författare)
  • Structural characterization of precious-mean quasiperiodic Mo/V single-crystal superlattices grown by dual-target magnetron sputtering
  • 1990
  • Ingår i: Physical Review B. - 1098-0121. ; 41:15, s. 10398-10407
  • Tidskriftsartikel (refereegranskat)abstract
    • A class of quasiperiodic superlattice structures, which can be generated by the concurrent inflation rule A→AmB and B→A (where m=positive integer), has been studied both theoretically and experimentally. Given that the ratios between the thicknesses of the two superlattice building blocks, A and B, are chosen to be γ(m)=[m+(m2+4)1/2]/2 (known as the ‘‘precious means’’), then the x-ray- and electron-diffraction peak positions are analytically found to be located at the wave vectors q=2πΛ−1r[γ(m)]k, where r and k are integers and Λ is an average superlattice wavelength. The analytically obtained results have been compared to experimental results from single-crystalline Mo/V superlattice structures, generated with m=1, 2, and 3. The superlattices were grown by dual-target dc-magnetron sputtering on MgO(001) substrates kept at 700 °C. X-ray diffraction (XRD) and selected-area electron diffraction (SAED) showed that the analytical model mentioned above predicts the peak positions of the experimental XRD and SAED spectra with a very high accuracy. Furthermore, numerical calculations of the diffraction intensities based on a kinematical model of diffraction showed good agreement with the experimental data for all three cases. In addition to a direct verification of the quasiperiodic modulation, both conventional and high-resolution cross-sectional transmission electron microscopy (XTEM) showed that the superlattices are of high crystalline quality with sharp interfaces. Based on lattice resolution images, the width of the interfaces was determined to be less than two (002) lattice-plane spacings (≊0.31 nm).
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-3 av 3

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy