1. |
- Wu, Zhongbin, et al.
(författare)
-
High-Performance Hybrid White Organic Light-Emitting Diodes with Superior Efficiency/Color Rendering Index/Color Stability and Low Efficiency Roll-Off Based on a Blue Thermally Activated Delayed Fluorescent Emitter
- 2016
-
Ingår i: Advanced Functional Materials. - : Wiley. - 1616-301X .- 1616-3028. ; 26:19, s. 3306-3313
-
Tidskriftsartikel (refereegranskat)abstract
- Thermally activated delayed fluorescence (TADF)-based white organic light-emitting diodes (WOLEDs) are highly attractive because the TADF emitters provide a promising alternative route to harvest triplet excitons. One of the major challenges is to achieve superior efficiency/color rendering index/color stability and low efficiency roll-off simultaneously. In this paper, high-performance hybrid WOLEDs are demonstrated by employing an efficient blue TADF emitter combined with red and green phosphorescent emitters. The resulting WOLED shows the maximum external quantum efficiency, current efficiency, and power efficiency of 23.0%, 51.0 cd A(-1), and 51.7 lm W-1, respectively. Moreover, the device exhibits extremely stable electroluminescence spectra with a high color rendering index of 89 and Commission Internationale de L'Eclairage coordinates of (0.438, 0.438) at the practical brightness of 1000 cd m(-2). The achievement of these excellent performances is systematically investigated by versatile experimental and theoretical evidences, from which it is concluded that the utilization of a blue-green-red cascade energy transfer structure and the precise manipulation of charges and excitons are the key points. It can be anticipated that this work might be a starting point for further research towards high-performance hybrid WOLEDs.
|
|
2. |
- Hu, Xianfeng, et al.
(författare)
-
Carbothermic reduction of synthetic chromite with/without the addition of iron powder
- 2016
-
Ingår i: ISIJ International. - : Iron and Steel Institute of Japan. - 0915-1559 .- 1347-5460. ; 56:12, s. 2147-2155
-
Tidskriftsartikel (refereegranskat)abstract
- Carbothermic reduction of chromite is an important industrial process for extracting chromium from the chromite. To have a better understanding of the effect of iron on the carbothermic reduction of chromite, the reduction of synthetic chromite (FeCr2O4) by graphite with/without the addition of iron powder was investigated in this paper by Thermogravimetric Analysis (TGA) in argon atmosphere. The fractional reduced samples were examined by SEM/EDS and XRD analysis, and the reduction process was thermodynamically and kinetically evaluated. The experimental results show that the iron powder addition enhances the reduction of FeCr2O4 and this effect increases when increased amounts of iron powder are added. This phenomenon is attributed to the in situ dissolution of chromium into the iron and mixed carbide (Cr,Fe)7C3, which can decrease the activity of the nascent chromium formed by the reduction of the FeCr2O4. The experimental results indicate that the reduction of FeCr2O4 with up to 80 wt.% iron powder addition is likely to be a single-step process and the kinetic analysis suggests that the reduction reaction is likely to be either (a) chemical reaction at the surface of FeCr2O4 or (b) diffusional dissolution of the product (FeCr2) into the iron/alloy particles or the mixed control of (a) and (b).
|
|
3. |
|
|
4. |
- Hu, Xianfeng
(författare)
-
Studies on Carbothermic Reduction of Chromite in the Presence of FeOx
- 2016
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Direct chromium alloying by chromite ore is a promising technology for producing Crcontainingsteels, as the ferrochrome production process and the chromium alloying processare integrated into a single step, which has the potential of saving energy and raw materials.In this work Thermogravimetric Analysis experiments and induction furnace experiments (upto 80-kg scale) have been carried out to investigate the carbothermic reduction process ofchromite in the presence of FeOx (iron, mill scale or magnetite). The aims are to investigatethe effect of FeOx on the carbothermic reduction of chromite and to explore the potential ofdirectly alloying steel with chromium by the designed alloying precursor ‘chromite ore +FeOx + carbonaceous material’.The results from the Thermogravimetric Analysis experiments show that FeOx can enhancethe carbothermic reduction of chromite and the enhancing effect increases when increasedamounts of FeOx are added to the chromite. The enhancing effect is attributed to the presenceof added metallic iron or the metallic iron reduced from mill scale or magnetite, which candecrease the activity of chromium by having chromium dissolve in the iron in situ. The resultsfrom the induction furnace experiments show that the steel can be directly alloyed withchromium by using the designed alloying precursor ‘chromite ore + mill scale + petroleumcoke’ and the chromium yield from chromite ore increases when increased amounts of millscale are added to the alloying precursor.The designed alloying precursor, on one hand, can be potentially used to directly alloy steelwith chromium in the Electric Arc Furnace steelmaking process and, on the other hand, can bepotentially used to produce Cr pre-alloyed iron powder or Cr pre-alloyed Direct Reduced Ironby the solid-state reduction process. The proposed applications have the potential to improvethe raw materials efficiency and energy efficiency.
|
|
5. |
- Hu, Xianfeng, et al.
(författare)
-
Thermal Analysis Study on the Carbothermic Reduction of Chromite Ore with the Addition of Mill Scale
- 2016
-
Ingår i: Steel Research International. - : Wiley-VCH Verlag. - 1611-3683 .- 1869-344X. ; 87:5, s. 562-570
-
Tidskriftsartikel (refereegranskat)abstract
- This paper presents a fundamental study on the carbothermic reduction of chromite ore with the addition of mill scale, which forms the basis for designing an alloying precursor, "chromite ore + mill scale + carbon," for direct chromium alloying. The reduction of chromite ore by petroleum coke with or without the addition of mill scale is investigated by Thermogravimetric Analysis (TGA) under non-isothermal conditions (from room temperature to 1823 K) in the argon atmosphere; the fractional reduced samples were characterized by SEM/EDS and XRD analyses. The experimental results show that the mill scale in the alloying mixture is reduced to high active iron first and disseminated around the chromite ore particles; the reduction of chromite ore is enhanced with the addition of mill scale especially at temperatures higher than 1623 K, and the enhancing effect increased with increasing mill scale addition. The enhancing effect is attributed to the presence of molten Fe-C alloy in the vicinity of chromite ore, which can decrease the thermodynamic activity of chromium by having chromium in situ dissolve into the melt. In this paper, the effect of mill scale addition on the reduction of chromite ore is investigated on the samples with three different amounts of mill scale addition (78 wt%, 38 wt%, and 0 for the samples #1b, #2b, and #3b, respectively) by thermogravimetric technique. The fractional reduced samples are characterized by SEM/EDS and XRD analyses. The mechanism of mill scale addition on the reduction of chromite ore is discussed and the industrial implications of the experimental results are also presented.
|
|
6. |
- Wu, Zhongbin, et al.
(författare)
-
Achieving Extreme Utilization of Excitons by an Efficient Sandwich-Type Emissive Layer Architecture for Reduced Efficiency Roll-Off and Improved Operational Stability in Organic Light-Emitting Diodes
- 2016
-
Ingår i: ACS Applied Materials and Interfaces. - : American Chemical Society (ACS). - 1944-8244 .- 1944-8252. ; 8:5, s. 3150-3159
-
Tidskriftsartikel (refereegranskat)abstract
- It has been demonstrated that the efficiency roll-off is generally caused by the accumulation of excitons or charge carriers, which is intimately related to the emissive layer (EML) architecture in organic light-emitting diodes (OLEDs). In this article, an efficient sandwich-type EML structure with a mixed-host EML sandwiched between two single-host EMLs was designed to eliminate this accumulation, thus simultaneously achieving high efficiency, low efficiency roll-off and good operational stability in the resulting OLEDs. The devices show excellent electroluminescence performances, realizing a maximum external quantum efficiency (EQE) of 24.6% with a maximum power efficiency of 105.6 lm W-1 and a maximum current efficiency of 93.5 cd A(-1). At the high brightness of 5 000 cd m(-2), they still remain as high as 23.3%, 71.1 lm W-1, and 88.3 cd A(-1), respectively. And, the device'lifetime is up to 2000 h at initial luminance of 1000 cd m(-2), which is significantly higher than that of compared devices with conventional EML structures. The improvement mechanism is systematically studied by the dependence of the exciton distribution in EML and the exciton quenching processes. It can be seen that the utilization of the efficient sandwich-type EML broadens the recombination zone width, thus greatly reducing the exciton quenching and increasing the probability of the exciton recombination. It is believed that the design concept, provides a new avenue for us to achieve high-performance OLEDs.
|
|