| 1. |
- Landälv, Ludvig, 1982-, et al.
(author)
-
Phase composition and transformations in magnetron-sputtered (Al,V)2O3 coatings
- 2019
-
In: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 688
-
Journal article (peer-reviewed)abstract
- Coatings of (Al1-xVx)2O3, with x ranging from 0 to 1, were deposited by pulsed DC reactive sputter deposition on Si(100) at a temperature of 550 °C. XRD showed three different crystal structures depending on V-metal fraction in the coating: α-V2O3 rhombohedral structure for 100 at.% V, a defect spinel structure for the intermediate region, 63–42 at.% V. At lower V-content, 18 and 7 at.%, a gamma-alumina-like solid solution was observed, shifted to larger d-spacing compared to pure γ-Al2O3. The microstructure changes from large columnar faceted grains for α-V2O3 to smaller equiaxed grains when lowering the vanadium content towards pure γ-Al2O3. Annealing in air resulted in formation of V2O5 crystals on the surface of the coating after annealing to 500 °C for 42 at.% V and 700 °C for 18 at.% V metal fraction respectively. The highest thermal stability was shown for pure γ-Al2O3-coating, which transformed to α-Al2O3 after annealing to 1100 °C. Highest hardness was observed for the Al-rich oxides, ~24 GPa. The latter decreased with increasing V-content, larger than 7 at.% V metal fraction. The measured hardness after annealing in air decreased in conjunction with the onset of further oxidation of the coatings.
|
|
| 2. |
- Magnuson, Martin, 1965-, et al.
(author)
-
Chemical Bonding in Epitaxial ZrB2 Studied by X-ray Spectroscopy
- 2018
-
In: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 649, s. 89-96
-
Journal article (peer-reviewed)abstract
- The chemical bonding in an epitaxial ZrB2 film is investigated by Zr K-edge (1s) X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies and compared to the ZrB2 compound target from which the film was synthesized as well as a bulk α-Zr reference. Quantitative analysis of X-ray Photoelectron Spectroscopy spectra reveals at the surface: ~5% O in the epitaxial ZrB2 film, ~19% O in the ZrB2 compound target and ~22% O in the bulk α-Zr reference after completed sputter cleaning. For the ZrB2 compound target, X-ray diffraction (XRD) shows weak but visible 11, 111, and 220 peaks from monoclinic ZrO2 together with peaks from ZrB2 and where the intensity distribution for the ZrB2 peaks show a randomly oriented target material. For the bulk α-Zr reference no peaks from any crystalline oxide were visible in the diffractogram recorded from the 0001-oriented metal. The Zr K-edge absorption from the two ZrB2 samples demonstrate more pronounced oscillations for the epitaxial ZrB2 film than in the bulk ZrB2 attributed to the high atomic ordering within the columns of the film. The XANES exhibits no pre-peak due to lack of p-d hybridization in ZrB2, but with a chemical shift towards higher energy of 4 eV in the film and 6 eV for the bulk compared to α-Zr (17.993 keV) from the charge-transfer from Zr to B. The 2 eV larger shift in bulk ZrB2 material suggests higher oxygen content than in the epitaxial film, which is supported by XPS. In EXAFS, the modelled cell-edge in ZrB2 is slightly smaller in the thin film (a=3.165 Å, c=3.520 Å) in comparison to the bulk target material (a=3.175 Å, c=3.540 Å) while in hexagonal closest-packed metal (α-phase, a=3.254 Å, c=5.147 Å). The modelled coordination numbers show that the EXAFS spectra of the epitaxial ZrB2 film is highly anisotropic with strong in-plane contribution, while the bulk target material is more isotropic. The Zr-B distance in the film of 2.539 Å is in agreement with the calculated value from XRD data of 2.542 Å. This is slightly shorter compared to that in the ZrB2 compound target 2.599 Å, supporting the XANES results of a higher atomic order within the columns of the film compared to bulk ZrB2.
|
|
| 3. |
- Magnuson, Martin, 1965-, et al.
(author)
-
Reactive magnetron sputtering of tungsten target in krypton/trimethylboron atmosphere
- 2019
-
In: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 688
-
Journal article (peer-reviewed)abstract
- W-B-C films were deposited on Si(100) substrates held at elevated temperature by reactive sputtering from a W target in Kr/trimethylboron (TMB) plasmas. Quantitative analysis by Xray photoelectron spectroscopy (XPS) shows that the films are W-rich between ~ 73 and ~ 93 at.% W. The highest metal content is detected in the film deposited with 1 sccm TMB. The C and B concentrations increase with increasing TMB flow to a maximum of ~18 and ~7 at.%, respectively, while the O content remains nearly constant at 2-3 at.%. Chemical bonding structure analysis performed after samples sputter-cleaning reveals C-W and B-W bonding and no detectable W-O bonds. During film growth with 5 sccm TMB and 500 o C or with 10 sccm TMB and 300-600 o C thin film X-ray diffraction shows the formation of cubic 100-oriented WC1-x with a possible solid solution of B. Lower flows and lower growth temperatures favor growth of W and W2C, respectively. Depositions at 700 and 800 o C result in the formation of WSi2 due to a reaction with the substrate. At 900 o C, XPS analysis shows ~96 at.% Si in the film due to Si interdiffusion. Scanning electron microscopy images reveal a fine-grained microstructure for the deposited WC1-x films. Nanoindentation gives hardness values in the range from ~23 to ~31 GPa and reduced elastic moduli between ~220 and 280 GPa in the films deposited at temperatures lower than 600 o C. At higher growth temperatures the hardness decreases by a factor of 3 to 4 following the formation of WSi2 at 700-800 o C and Si-rich surface at 900 o C.
|
|
| 4. |
- Serban, Elena Alexandra, 1988-, et al.
(author)
-
Site-controlled growth of GaN nanorod arrays by magnetron sputter epitaxy
- 2018
-
In: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 660, s. 950-955
-
Journal article (peer-reviewed)abstract
- Catalyst-free GaN nanorod regular arrays have been realized by reactive magnetron sputter epitaxy. Two nanolithographic methods, nanosphere lithography (NSL) and focused ion beam lithography (FIBL), were applied to pattern Si substrates with TiNx masks. The growth temperature was optimized for achieving selectivity and well-faceted nanorods grown onto the NSL-patterned substrates. With increasing temperature from 875 to 985 °C, we observe different growth behaviors and associate them with selective insensitive, diffusion-dominated, and desorption-dominated zones. To further achieve site-specific and diameter control, these growth parameters were transferred onto FIBL-patterned substrates. Further investigation into the FIBL process through tailoring of milling current and time in combination with varying nanorod growth temperature, suggests that minimization of mask and substrate damage is the key to attain uniform, well-defined, single, and straight nanorods. Destruction of the mask results in selective area growth failure, while damage of the substrate surface promotes inclined nanorods grown into the openings, owning to random oriented nucleation.
|
|