| 1. |
- Agostini, Marco, 1987, et al.
(författare)
-
Designing a Safe Electrolyte Enabling Long‐Life Li/S Batteries
- 2019
-
Ingår i: ChemSusChem. - : Wiley. - 1864-5631 .- 1864-564X. ; 12:18, s. 4176-4184
-
Tidskriftsartikel (refereegranskat)abstract
- Lithium–sulfur (Li/S) batteries suffer from “shuttle” reactions in which soluble polysulfide species continuously migrate to and from the Li metal anode. As a consequence, the loss of active material and reactions at the surface of Li limit the practical applications of Li/S batteries. LiNO3 has been proposed as an electrolyte additive to reduce the shuttle reactions by aiding the formation of a stable solid electrolyte interphase (SEI) at the Li metal, limiting polysulfide shuttling. However, LiNO3 is continuously consumed during cycling, especially at low current rates. Therefore, the Li/S battery cycle life is limited by the LiNO3 concentration in the electrolyte. In this work, an ionic liquid (IL) [N-methyl-(n-butyl)pyrrolidinium bis(trifluoromethylsulfonyl)imide] was used as an additive to enable longer cycle life of Li/S batteries. By tuning the IL concentration, an enhanced stability of the SEI and lower flammability of the solutions were demonstrated, that is, higher safety of the battery. The Li/S cell built with a high sulfur mass loading (4 mg cm−2) and containing the IL-based electrolyte demonstrated a stable capacity of 600 mAh g−1 for more than double the number of cycles of a cell containing LiNO3 additive.
|
|
| 2. |
- Lim, Du Hyun, 1983, et al.
(författare)
-
Tailor-Made Electrospun Multilayer Composite Polymer Electrolytes for High-Performance Lithium Polymer Batteries
- 2018
-
Ingår i: Journal of Nanoscience and Nanotechnology. - : American Scientific Publishers. - 1533-4880. ; 18:9, s. 6499-6505
-
Tidskriftsartikel (refereegranskat)abstract
- A novel tailor-made multilayer composite polymer electrolyte, consisting of two outer layers of electrospun polyacrylonitrile (PAN) and one inner layer of poly(vinyl acetate) (PVAc)/poly(methyl methacrylate) (PMMA)/poly(ethylene oxide) (PEO) fibrous membrane, was prepared using continuous electrospinning. These membranes, which are made up of fibers with diameters in the nanometer range, were stacked in layers to produce interconnected pores that result in a high porosity. Gel polymer electrolytes (GPEs) were prepared by entrapping a liquid electrolyte (1 M LiPF6 in ethylene carbonate/dimethyl carbonate) in the membranes. The composite membranes exhibited a high electrolyte uptake of 450-510%, coupled with an improved room temperature ionic conductivity of up to 4.72 mS cm(-1) and a high electrochemical stability of 4.6 V versus Li/Li+. Electrochemical investigations of a composite membrane of PAN-PVAc-PAN, with a LiFePO4 cathode synthesized in-house, showed a high initial discharge capacity of 145 mAh g(-1), which corresponds to 85% utilization of the active material, and displayed stable cycle performance.
|
|