| 1. |
- Andersons, J., et al.
(författare)
-
Apparent interfacial shear strength of short-flax-fiber/starch acetate composites
- 2016
-
Ingår i: International Journal of Adhesion and Adhesives. - : Elsevier Ltd. - 0143-7496 .- 1879-0127. ; 64, s. 78-85
-
Tidskriftsartikel (refereegranskat)abstract
- The paper deals with an indirect industry-friendly method for identification of the interfacial shear strength (IFSS) in a fully bio-based composite. The IFSS of flax fiber/starch acetate is evaluated by a modified Bowyer and Bader method based on an analysis of the stress-strain curve of a short-fiber-reinforced composite in tension. A shear lag model is developed for the tensile stress-strain response of short-fiber-reinforced composites allowing for an elastic-perfectly plastic stress transfer. Composites with different fiber volume fractions and a variable content of plasticizer have been analyzed. The apparent IFSS of flax/starch acetate is within the range of 5.5-20.5 MPa, depending on composition of the material. The IFSS is found to be greater for composites with a higher fiber loading and to decrease with increasing content of plasticizer. The IFSS is equal or greater than the yield strength of the neat polymer, suggesting good adhesion, as expected for the chemically compatible constituents.
|
|
| 2. |
- Andersons, J., et al.
(författare)
-
Scale effect of the tensile strength of flax-fabric-reinforced polymer composites
- 2011
-
Ingår i: Journal of reinforced plastics and composites (Print). - : SAGE Publications. - 0731-6844 .- 1530-7964. ; 30:23, s. 1969-1974
-
Tidskriftsartikel (refereegranskat)abstract
- The development of UD natural fiber composites, considered for application as structural materials, necessitates evaluation of the scale effect of their strength. Alignment of the fibers in flax bast fiber composites can be achieved by employing textile reinforcement, such as yarns and fabrics. Cutting specimens for mechanical tests out of such textile-reinforced composite plates results in a complex non-uniform reinforcement structure at their edges, which may affect the strength of specimens. Scale effect of the tensile strength in the fiber direction of flax-fabric-reinforced composites is studied in the current work. A model accounting for both volume and edge effect of the specimens on their tensile strength is proposed. © The Author(s) 2011.
|
|