- Graphene is the first single-atom-thick two-dimensional material and exhibits a large set of interesting properties. This thesis consists of two parts. The first regards the growth of large-area graphene using chemical vapor deposition (CVD). Graphene is grown using CVD on copper catalyst showing high quality with charge carrier mobility exceeding 3000 cm2/Vs.Wet chemical etching is used to transfer graphene to insulating substrates. Cu is removed using either diluted HNO3 or diluted HCl with a small amount of added H2O2. To allow for faster transfer and avoid consuming copper, a hydrogen-bubbling method is developed to delaminate graphene from Cu. Graphene transferred this way shows properties similar to those of graphene transferred using wet etching.To avoid transfer-related issues, graphene is grown non-catalytically directly on insulating substrates such as SiO2, Al2O3, and Si3N4. The grain size is only ~10 nm due to the lack of catalytic activity during growth. Such graphene shows inferior electronic properties with mobility in the order of ~tens of cm2/Vs. Despite that, sheet resistance around kΩ, the possibility to grow several layer thick films, and optical properties similar to those of pristine graphene make it an interesting material.A method for cleaning graphene mechanically using atomic force microscopy (AFM) is developed. By appropriate choice of the applied force, atomically smooth (roughness
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Nanoteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Nano-technology (hsv//eng)
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Keyword
- Graphene
- Atomic force microscopy
- Aharonov-Bohm effect
- Weak localization
- Bolometer
- Chemical vapor deposition
- Synthesis
- Mechanical cleaning
Publication and Content Type
- dok (subject category)
- vet (subject category)
Find in a library
To the university's database