- Aksenova, N.A., et al.
(författare)
-
Structure studies of C60 polymerized at low pressures
- 1997
-
Ingår i: Fullerenes. - Pennington, NJ : The Electrochemical Society. - 1566771927 ; , s. 687-694
-
Konferensbidrag (refereegranskat)abstract
- The structure and lattice properties of a polymerized C60 sample were investigated by X-ray powder diffraction over the range from liquid-nitrogen to room temperature. The aim of these studies was to establish the effect of low-pressure compression (up to 1.1 GPa) on the phase composition of the sample, to determine the structure of the phases involved, to obtain the variation of the lattice parameters with temperature, to observe eventual phase transformation in polymerized C60, and to elucidate the evolution of the orientational order with varying temperature. Analysis of the room-temperature diffraction patterns indicates that the sample contained at least two major phases, namely rhombohedral and and tetragonal with the polymerization array close to two-dimensional. Our data obtained on samples annealed at 300 C in the air allow us to conclude that polymerized C60 converts to a mixture of the fcc structure plus a new phase, presumably C60O.
|
|
| 2. |
- Aleksandrovskii, A. N., et al.
(författare)
-
Negative thermal expansion of fullerite C60 at helium temperatures
- 1997
-
Ingår i: Low temperature physics (Woodbury, N.Y., Print). - : AIP Publishing. - 1063-777X .- 1090-6517. ; 23:11, s. 943-946
-
Tidskriftsartikel (refereegranskat)abstract
- The thermal expansion of fullerite C60 has been measured in the temperature range 2–9 K. A compacted fullerite sample with a diameter of about 6 mm and height of 2.4 mm was used. It was found that at temperatures below ~ 3.4 K the linear thermal expansion coefficient becomes negative. At temperatures above 5 K our results are in good agreement with the available literature data. A qualitative explanation of the results is proposed
|
|
| 3. |
- Aleksandrovskii, A. N., et al.
(författare)
-
Thermal expansion of single-crystal fullerite C60 at helium temperatures
- 2000
-
Ingår i: Low temperature physics (Woodbury, N.Y., Print). - : AIP Publishing. - 1063-777X .- 1090-6517. ; 26:1, s. 75-80
-
Tidskriftsartikel (refereegranskat)abstract
- The thermal expansion of single-crystal fullerite C60 has been studied in the range of liquid-helium temperatures (2–10 K). At temperatures below ~4.5 K the thermal expansion of fullerite C60 becomes negative, in agreement with the previous results on polycrystalline materials. A qualitative explanation of the results is proposed.
|
|
| 4. |
- Lundin, Anders, et al.
(författare)
-
Compressibility of C61D2 up to 1 GPa in the temperature range 175 - 345 K
- 1996
-
Ingår i: Carbon. - : Elsevier Science Ltd.. - 0008-6223 .- 1873-3891. ; 34:9, s. 1119-1121
-
Tidskriftsartikel (refereegranskat)abstract
- We have measured the bulk modulus K for C61D2 up to 1 GPa in the temperature range 175–343 K. For face-centered cubic C61D2 above 290 K, we find an anomalously low value for K below about 0.15 GPa, possibly indicating pressure-induced changes in the structure. The (extrapolated) zero-p bulk modulus K(0) decreases with increasing T from 6.7 GPa at 175 K to 5.2 GPa at 343 K. A comparison with hypothetical expanded f.c.c. C60 with the same lattice constant shows that K(0) values are similar, indicating that the main intermolecular interactions are still between molecular bellies, not the sidegroups.
|
|