Enhanced ductility and strength in a cast Al–Mg alloy with high Mg content

• Cast Al–Mg alloys with high Mg content have attracted considerable interest as a result of exceptionally low mass density and enhanced Mg solid-solution strengthening effect. However, poor ductility in this class of cast Al–Mg alloys originating from the increased amount of brittle Al3Mg2 phase presents a challenge. This work aims to improve ductility of a cast Al-10 wt%Mg alloy by prolonging time and/or increasing temperature during solid-solution treatment, hence minimizing the amount of the Al3Mg2 phase. The amounts of Al3Mg2 decrease and the concentrations of solute Mg increase with prolonging time and/or increasing temperature, improving both ductility and strength. Solid-solution treatment at 425 °C for 9 h or at 438 °C for 3 h induces complete dissolution of the Al3Mg2 phase, achieving an average uniform elongation of ~27% accompanied by an average 0.2% offset yield strength of ~186 MPa. The mechanisms improving both ductility and strength are discussed. 

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

Aluminum alloys

Casting

Ductility

Solid-solution treatment

Strength

Binary alloys

Solid solutions

Temperature

Complete dissolution

Enhanced ductility

Increasing temperatures

Mg content

Phase present

Solid solution strengthening

Solid solution treatment

Uniform elongation

Magnesium alloys

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)