TEM study of the early stages of the precipitation process in strip-cast Al3003 alloys
- 1992
-
Ingår i: Journal of Materials Research. - 0884-2914. ; 7, s. 3235-3241
-
Tidskriftsartikel (refereegranskat)abstract
- The precipitation behavior, especially the early nucleation stages, of the industrial strip-cast Al3003 alloys was investigated by using transmission electron microscopy (TEM). An icosahedral quasicrystalline phase was found as secondary particles in these strip-cast alloys after heat treatment for a few seconds. Three different nucleation paths are proposed based on the TEM observations. They have the same origin, viz. (Mn, Fe)-containing Mackay icosahedra, and are governed by the composition of alloys, especially the Mn and Si content.
|
|