| 1. |
- Ahniyaz, Anwar, et al.
(författare)
-
Preparation of iron oxide nanocrystals by surfactant-free or oleic acid-assisted thermal decomposition of a Fe(III) alkoxide
- 2008
-
Ingår i: Journal of Magnetism and Magnetic Materials. - : Elsevier BV. - 0304-8853 .- 1873-4766. ; 320:6, s. 781-787
-
Tidskriftsartikel (refereegranskat)abstract
- A new non-hydrolytic, alkoxide-based route was developed to synthesize iron oxide nanocrystals. Surfactant-free thermal decomposition of the iron 2-methoxy-ethoxide precursors results in the formation of uniform iron oxide nanocrystals with an average size of 5.6 nm. Transmission electron microscope study shows that the nanocrystals are protected against aggregation by a repulsive surface layer, probably originating from the alkoxy-alkoxide ligands. Addition of oleic acid resulted in monodisperse nanocrystals with an average size of 4 nm. Mössbauer analysis confirmed that the nanocrystals mainly consisted of maghemite. Analysis of the magnetic hysteresis loop measurements and the zero field and field cooled measurements displayed an excellent fit to established theories for single-domain superparamagnetic nanocrystals and the size of the magnetic domains correlated well to the crystallite size obtained from transmission electron microscope.
|
|
| 2. |
- Ahrentorp, Fredrik, et al.
(författare)
-
Effective particle magnetic moment of multi-core particles
- 2015
-
Ingår i: Journal of Magnetism and Magnetic Materials. - : Elsevier BV. - 0304-8853 .- 1873-4766. ; 380, s. 221-226
-
Tidskriftsartikel (refereegranskat)abstract
- In this study we investigate the magnetic behavior of magnetic multi-core particles and the differences in the magnetic properties of multi-core and single-core nanoparticles and correlate the results with the nanostructure of the different particles as determined from transmission electron microscopy (TEM). We also investigate how the effective particle magnetic moment is coupled to the individual moments of the single-domain nanocrystals by using different measurement techniques: DC magnetometry, AC susceptometry, dynamic light scattering and TEM. We have studied two magnetic multi-core particle systems BNF Starch from Micromod with a median particle diameter of 100 am and FeraSpin R from nanoPET with a median particle diameter of 70 nm - and one single-core particle system - SHP25 from Ocean NanoTech with a median particle core diameter of 25 nm. (C) 2014 Elsevier B.V. All rights reserved.
|
|
| 3. |
|
|
| 4. |
- Baresel, Christian, et al.
(författare)
-
Functionalized magnetic particles for water treatment
- 2019
-
Ingår i: Heliyon. - : Elsevier BV. - 2405-8440. ; 5:8
-
Tidskriftsartikel (refereegranskat)abstract
- In this study, we have taken the concept of water treatment by functionalized magnetic particles one step forward by integrating the technology into a complete proof of concept, which included the preparation of surface modified beads, their use as highly selective absorbents for heavy metals ions (Zinc, Nickel), and their performance in terms of magnetic separation. The separation characteristics were studied both through experiments and by simulations. The data gathered from these experimental works enabled the elaboration of various scenarios for Life Cycle Analysis (LCA). The LCA showed that the environmental impact of the system is highly dependent on the recovery rate of the magnetic particles. The absolute impact on climate change varied significantly among the scenarios studied and the recovery rates. The results support the hypothesis that chelation specificity, magnetic separation and bead recovery should be optimized to specific targets and applications.
|
|
| 5. |
- Bender, P., et al.
(författare)
-
Dipolar-coupled moment correlations in clusters of magnetic nanoparticles
- 2018
-
Ingår i: Physical Review B. - 2469-9950 .- 2469-9969. ; 98:22
-
Tidskriftsartikel (refereegranskat)abstract
- Here, we resolve the nature of the moment coupling between 10-nm dimercaptosuccinic acid-coated magnetic nanoparticles. The individual iron oxide cores were composed of >95% maghemite and agglomerated to clusters. At room temperature the ensemble behaved as a superparamagnet according to Mössbauer and magnetization measurements, however, with clear signs of dipolar interactions. Analysis of temperature-dependent ac susceptibility data in the superparamagnetic regime indicates a tendency for dipolar-coupled anticorrelations of the core moments within the clusters. To resolve the directional correlations between the particle moments we performed polarized small-angle neutron scattering and determined the magnetic spin-flip cross section of the powder in low magnetic field at 300 K. We extract the underlying magnetic correlation function of the magnetization vector field by an indirect Fourier transform of the cross section. The correlation function suggests nonstochastic preferential alignment between neighboring moments despite thermal fluctuations, with anticorrelations clearly dominating for next-nearest moments. These tendencies are confirmed by Monte Carlo simulations of such core clusters.
|
|
| 6. |
- Bender, P., et al.
(författare)
-
Influence of clustering on the magnetic properties and hyperthermia performance of iron oxide nanoparticles
- 2018
-
Ingår i: Nanotechnology. - : IOP Publishing. - 0957-4484 .- 1361-6528. ; 29:42
-
Tidskriftsartikel (refereegranskat)abstract
- Clustering of magnetic nanoparticles can drastically change their collective magnetic properties, which in turn may influence their performance in technological or biomedical applications. Here, we investigate a commercial colloidal dispersion (FeraSpin™R), which contains dense clusters of iron oxide cores (mean size around 9 nm according to neutron diffraction) with varying cluster size (about 18-56 nm according to small angle x-ray diffraction), and its individual size fractions (FeraSpin™XS, S, M, L, XL, XXL). The magnetic properties of the colloids were characterized by isothermal magnetization, as well as frequency-dependent optomagnetic and AC susceptibility measurements. From these measurements we derive the underlying moment and relaxation frequency distributions, respectively. Analysis of the distributions shows that the clustering of the initially superparamagnetic cores leads to remanent magnetic moments within the large clusters. At frequencies below 105 rad s-1, the relaxation of the clusters is dominated by Brownian (rotation) relaxation. At higher frequencies, where Brownian relaxation is inhibited due to viscous friction, the clusters still show an appreciable magnetic relaxation due to internal moment relaxation within the clusters. As a result of the internal moment relaxation, the colloids with the large clusters (FS-L, XL, XXL) excel in magnetic hyperthermia experiments.
|
|
| 7. |
- Bender, P., et al.
(författare)
-
Relating Magnetic Properties and High Hyperthermia Performance of Iron Oxide Nanoflowers
- 2018
-
Ingår i: Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 122:5, s. 3068-3077
-
Tidskriftsartikel (refereegranskat)abstract
- We investigated, in depth, the interrelations among structure, magnetic properties, relaxation dynamics and magnetic hyperthermia performance of magnetic nanoflowers. The nanoflowers are about 39 nm in size, and consist of densely packed iron oxide cores. They display a remanent magnetization, which we explain by the exchange coupling between the cores, but we observe indications for internal spin disorder. By polarized small-angle neutron scattering, we unambiguously confirm that, on average, the nanoflowers are preferentially magnetized along one direction. The extracted discrete relaxation time distribution of the colloidally dispersed particles indicates the presence of three distinct relaxation contributions. We can explain the two slower processes by Brownian and classical Néel relaxation, respectively. The additionally observed very fast relaxation contributions are attributed by us to the relaxation of disordered spins within the nanoflowers. Finally, we show that the intrinsic loss power (ILP, magnetic hyperthermia performance) of the nanoflowers measured in colloidal dispersion at high frequency is comparatively large and independent of the viscosity of the surrounding medium. This concurs with our assumption that the observed relaxation in the high frequency range is primarily a result of internal spin relaxation, and possibly connected to the disordered spins within the individual nanoflowers.
|
|
| 8. |
- Bogren, Sara, et al.
(författare)
-
Classification of Magnetic Nanoparticle Systems—Synthesis, Standardization and Analysis Methods in the NanoMag Project
- 2015
-
Ingår i: International Journal of Molecular Sciences. - : MDPI AG. - 1661-6596 .- 1422-0067. ; 16:9, s. 20308-20325
-
Tidskriftsartikel (refereegranskat)abstract
- This study presents classification of different magnetic single- and multi-core particle systems using their measured dynamic magnetic properties together with their nanocrystal and particle sizes. The dynamic magnetic properties are measured with AC (dynamical) susceptometry and magnetorelaxometry and the size parameters are determined from electron microscopy and dynamic light scattering. Using these methods, we also show that the nanocrystal size and particle morphology determines the dynamic magnetic properties for both single- and multi-core particles. The presented results are obtained from the four year EU NMP FP7 project, NanoMag, which is focused on standardization of analysis methods for magnetic nanoparticles.
|
|
| 9. |
- Burger, Paul, 1997, et al.
(författare)
-
Atomic Force Manipulation of Single Magnetic Nanoparticles for Spin-Based Electronics
- 2022
-
Ingår i: ACS Nano. - : American Chemical Society. - 1936-0851 .- 1936-086X. ; 16:11, s. 19253-19260
-
Tidskriftsartikel (refereegranskat)abstract
- Magnetic nanoparticles (MNPs) are instrumental for fabrication of tailored nanomagnetic structures, especially where top-down lithographic patterning is not feasible. Here, we demonstrate precise and controllable manipulation of individual magnetite MNPs using the tip of an atomic force microscope. We verify our approach by placing a single MNP with a diameter of 50 nm on top of a 100 nm Hall bar fabricated in a quasi-two-dimensional electron gas (q2DEG) at the oxide interface between LaAlO3 and SrTiO3 (LAO/STO). A hysteresis loop due to the magnetic hysteresis properties of the magnetite MNPs was observed in the Hall resistance. Further, the effective coercivity of the Hall resistance hysteresis loop could be changed upon field cooling at different angles of the cooling field with respect to the measuring field. The effect is associated with the alignment of the MNP magnetic moment along the easy axis closest to the external field direction across the Verwey transition in magnetite. Our results can facilitate experimental realization of magnetic proximity devices using single MNPs and two-dimensional materials for spin-based nanoelectronics. © 2022 The Authors.
|
|
| 10. |
- Chakkarapani, Prabu, et al.
(författare)
-
Encapsulation of methotrexate loaded magnetic microcapsules for magnetic drug targeting and controlled drug release
- 2015
-
Ingår i: Journal of Magnetism and Magnetic Materials. - : Elsevier BV. - 0304-8853 .- 1873-4766. ; 380, s. 285-294
-
Tidskriftsartikel (refereegranskat)abstract
- We report on the development and evaluation of methotrexate magnetic microcapsules (MMC) for targeted rheumatoid arthritis therapy. Methotrexate was loaded into CaCO3-PSS (poly (sodium 4-styrenesulfonate)) doped microparticles that were coated successively with poly (allylamine hydrochloride) and poly (sodium 4-styrenesulfonate) by layer-by-layer technique. Ferrofluid was incorporated between the polyelectrolyte layers. CaCO3-PSS core was etched by incubation with EDTA yielding spherical MMC. The MMC were evaluated for various physicochemical, pharmaceutical parameters and magnetic properties. Surface morphology, crystallinity, particle size, zeta potential, encapsulation efficiency, loading capacity, drug release pattern, release kinetics and AC susceptibility studies revealed spherical particles of ~3 µm size were obtained with a net zeta potential of +24.5 mV, 56% encapsulation and 18.6% drug loading capacity, 96% of cumulative drug release obeyed Hixson-Crowell model release kinetics. Drug excipient interaction, surface area, thermal and storage stability studies for the prepared MMC was also evaluated. The developed MMC offer a promising mode of targeted and sustained release drug delivery for rheumatoid arthritis therapy.
|
|