Hardness, elastic modulus and refractive index of oxynitride glasses prepared from woody biofuel ashes

• This paper reports the hardness, elastic modulus and refractive index values of the oxynitride glasses prepared from woody biofuel ashes. The glasses were prepared in nitrogen atmosphere at 1350-1500°C with addition of Ca metal as a precursor to the extra addition of this modifier. The glasses were homogenous, but appeared translucent grey to black. They contained up to 23 eq% of Ca and 5 eq% of N. The glass densities vary slightly between 2·76 to 2·92 g/cm3. The molar volume and compactness values vary between 8·01 cm3/mol to 8·31 cm3/mol and 0·446 to 0·462 respectively. Mechanical properties like hardness and reduced elastic modulus show values, up to 10 and 105 GPa, respectively. These properties are strongly correlated with the amount of N in the glass. The refractive index (1·54-1·75) increases with increasing N and Ca contents.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

Nyckelord

Biofuels

Calcium

Elastic moduli

Glass

Hardness

Nitrides

Biofuel ashes

Glass density

Nitrogen atmospheres

Oxynitride glass

Reduced elastic modulus

Refractive index

Glasteknologi

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)