Influence of Heat Treatments on Heat Affected Zone Cracking of Gas Tungsten Arc Welded Additive Manufactured Alloy 718
-
- Raza, Tahira, 1972- (författare)
- Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW
-
- Hurtig, Kjell, 1960- (författare)
- Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW
-
- Asala, Gbenga (författare)
- University of Manitoba, Department of Mechanical Engineering, Winnipeg, MB R3T 5V6, Canada
-
visa fler...
-
- Andersson, Joel, 1981- (författare)
- Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW
-
- Svensson, Lars-Erik, 1951- (författare)
- Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW
-
- Ojo, Olanrewaju Akanbi (författare)
- University of Manitoba, Department of Mechanical Engineering, Winnipeg, MB R3T 5V6, Canada
-
visa färre...
-
(creator_code:org_t)
- 2019-08-10
- 2019
- Engelska.
-
Ingår i: Metals. - : MDPI. - 2075-4701. ; 9:8
- Relaterad länk:
-
https://doi.org/10.3...
-
visa fler...
-
https://hv.diva-port... (primary) (Raw object)
-
https://www.mdpi.com...
-
https://urn.kb.se/re...
-
https://doi.org/10.3...
-
visa färre...
Abstract
Ämnesord
Stäng
- The weldability of additive manufactured Alloy 718 was investigated in various heat-treated conditions. The microstructure of the base metal was examined in detail in order to understand the effect of different pre-weld heat treatments; i.e., solution, solution and aging, and hot isostatic pressing. After welding, the variation in total crack lengths, maximum crack length and the total number of cracks in the heat affected zone (HAZ) were used as criteria for the cracking susceptibility of each material condition where wrought Alloy 718 was used as the reference material. Selective laser melting (SLM) manufactured Alloy 718 was susceptible to HAZ cracking in all material conditions. Total crack lengths in HAZ were highest in the SLM as-built condition and lowest in the SLM hot isostatic pressed condition. The cracks that were found in the HAZ of the welded materials consisted of liquation cracks, with eutectic product surrounding the cracks, as well as cracks from which liquation products were absent.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- selective laser melting; Alloy 718; heat treatments; gas tungsten arc welding; heat affected zone cracking
- Manufacturing and materials engineering
- Produktions- och materialteknik
- Production Technology
- Produktionsteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
-
Metals
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas