Investigation of forming quality and failure behaviours of multilayered welded joints using ultrasonic double roller welding
-
- Abbas, Zeshan (författare)
- Shenzhen Polytechnic University, China
-
- Zhao, Lun (författare)
- Shenzhen Polytechnic University, China
-
- Su, Jianxiong (författare)
- Shenzhen Polytechnic University, China
-
visa fler...
-
- Zhang, Peng (författare)
- Shenzhen Polytechnic University, China
-
- Deng, Jianxiong (författare)
- Shenzhen Polytechnic University, China
-
- Jiaqi, Zeng (författare)
- Shenzhen Polytechnic University, China
-
- Patel, Vivek (författare)
- University West
-
- Saboor, Hafiz Abdul (författare)
- Shanghai University, China
-
- Islam, Md. Shafiqul, 1984- (författare)
- Blekinge Tekniska Högskola,Institutionen för maskinteknik
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2024
- 2024
- Engelska.
-
Ingår i: Alexandria Engineering Journal. - : Elsevier. - 1110-0168 .- 2090-2670. ; 107, s. 491-506
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://bth.diva-por... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Ultrasonic metal welding machines are suitable for various complex applications (e.g., battery tabs) through unique mechanical design, special pressure application methods and high-precision welding. This work reports the weldability, forming quality and fractographic analysis of copper multilayered welded joints which were studied by SEM-EDS characterization, micro-hardness testing and tensile testing based on ultrasonic double roller welding (UDRW). Three groups of process parameters (A, B and C) were established to investigate the performance, production quality and welded joint surface interconnections. The tensile testing results of sample under parameter 3 in group A [S-P3(A)] indicate the maximum tensile strength of 69.859 N in T-peel test while the average tensile strength has increased by 58.525 N due to rise in welding time from 2 sec to 5 sec. The results analysis indicates that welding quality features in S-P3(A) joints under 4 bar, 100 mm/s, 45 % have been exploited. The over-welded zone was transformed into good-welded zone. The micro-cracks, fatigue stations and peeling texture in multilayers were reduced. It was found that when the welding energy was 10000 J then the tearing edges and interlayers cracks were minimized while keeping the other parameters constant. Moreover, when the amplitude increased up to 50 %, then numerous micro-cracks and micro-fissure stations were created, which leads to the occurrence of fracture in multi-layer welded joint. The EDS study investigated that the complex features are formed at the interface junction of sample 3 S3(A) in multilayer welds. The complex multilayer microstructures can induce and produce unique hardness properties for battery manufacturing. It leads to high quality and durable welds. Eventually, it is experimentally demonstrated that robust 40 layer welded joints can be obtained by the UDRW process. Data availability: The datasets used and/or analyzed during the current study are available from the corresponding author upon reasonable request. © 2024 The Authors
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- 40 layers
- Copper foils
- Lithium-ion batteries
- Mechanical testing
- SEM and EDS analysis
- Ultrasonic double roller welding
- Copper
- Cracks
- Ductile fracture
- Microhardness
- Rollers (machine components)
- Tensile strength
- Tensile testing
- Textures
- Ultrasonic testing
- 40 layer
- Complex applications
- Failure behaviors
- Forming quality
- Micro cracks
- Multi-layered
- Ultrasonic metal welding
- Welds