Dynamic Coarsening of Austenite Dendrite in Lamellar Cast Iron Part 2 – The influence of carbon composition

Investigation of dynamic coarsening in lamellar cast iron is extended over a wide interval ranging from hypoeutectic to eutectic composition. The dendrite morphology is defined on as-cast samples produced under various cooling rates. The as-cast morphology is considered being close to the one at the end of solidification. The obtained relations describing the coarsening process as a function of local solidification time and fraction austenite are compared to results obtained from interrupted solidification experiments. By using the Modulus of primary dendrite (MPD) and the Hydraulic diameter of the interdendritic space (DHyd IP) become possible to characterize the coarseness of a wide range of lamellar cast irons solidified under various cooling rates.

Lora, RubenJönköping University,JTH. Forskningsmiljö Material och tillverkning – Gjutning,Foundry Technology,Jönköping University, Sweden(Swepub:hj)loru (författare)
Diószegi, Attila,1962-Jönköping University,JTH. Forskningsmiljö Material och tillverkning – Gjutning,Jönköping University, Sweden(Swepub:hj)diat (författare)
RISESWECAST (creator_code:org_t)

Ingår i:Materials Science Forum: Trans Tech Publications790-791, s. 211-216, s. 211-2160255-54761662-9752
Ingår i:Materials Science Forum: Trans Tech Publications790-791, s. 211-216, s. 211-2169783038350934

Av författaren/redakt...: Fourlakidis, Vas ...; Lora, Ruben; Diószegi, Attila ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.