Microstructural response of various chromium carbide based coatings to erosion and nano impact testing
- Artikel/kapitelEngelska2017
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2017
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:hv-11399
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-11399URI
-
https://doi.org/10.1016/j.wear.2017.06.002DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
In this study, we demonstrate the microstructure dependency of erosion behaviour of laser clad, detonation sprayed and atmospheric plasma sprayed chromium carbide based coatings. The final chromium carbide content in all the coatings was a strong function of rapid solidification rate associated with the processes. In the laser clad coating majority of the chromium carbides re-solidified while in the thermally sprayed coatings chromium carbide re-solidification was hindered to a large extent. Hence, the final chromium carbide content in the thermally sprayed coating decreased with increased extent of particle melting during spraying. Decarburisation and oxidation during thermal spraying lead to the formation of chromium carbides with lower carbon content and chromium oxide(s). Laser clad and detonation sprayed coatings, with higher chromium carbide content, showed lower erosion rates and exhibited fewer brittle erosion events. Embrittlement due to excessive dissolution of chromium carbides into the matrix and poor splat bonding were found to be the reasons for higher erosion rate of the plasma sprayed coating. Scanning electron microscopy and quantification of single erodent impact events clearly established ductile material removal in the laser clad and detonation sprayed coating and brittle material removal in the plasma sprayed coating as the dominant mechanism(s). A good agreement was found between solid particle erosion testing and nano impact testing results.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Pitchuka, Suresh BabuInternational Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005, India
(författare)
-
Sivakumar, G.International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005, India
(författare)
-
Gundakaram, Ravi C.International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005, India
(författare)
-
Joshi, Shrikant V.,1960-Högskolan Väst,Forskningsmiljön produktionsteknik(PTW),Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW(Swepub:hv)shrjos
(författare)
-
Samajdar, I.Department of Metallurgical Engineering & Materials Science, IIT Bombay, Powai, Mumbai 400076, India
(författare)
-
International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005, India.International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005, India
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Wear: Elsevier BV386-387, s. 72-790043-16481873-2577
Internetlänk
Hitta via bibliotek
-
Wear
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas