Effect of water vapor on the oxidation behavior of HVAF-sprayed NiCr and NiCrAlY coatings
-
- Sadeghimeresht, Esmaeil, 1985- (författare)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West
-
- Eklund, Johan, 1991 (författare)
- Chalmers University of Technology, Department of Environmental Inorganic Chemistry, 41296 Gothenburg, Sweden,Chalmers tekniska högskola
-
- Phother Simon, Julien, 1991 (författare)
- Chalmers University of Technology, Department of Environmental Inorganic Chemistry, 41296 Gothenburg, Sweden,Chalmers tekniska högskola
-
visa fler...
-
- Liske, Jesper, 1978 (författare)
- Chalmers University of Technology, Department of Environmental Inorganic Chemistry, 41296 Gothenburg, Sweden,Chalmers tekniska högskola
-
- Markocsan, Nicolaie, 1967- (författare)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West
-
- Joshi, Shrikant V., 1960- (författare)
- Högskolan Väst,Forskningsmiljön produktionsteknik(PTW),PTW,University West
-
visa färre...
-
(creator_code:org_t)
- 2018-05-25
- 2018
- Engelska.
-
Ingår i: Materials and corrosion - Werkstoffe und Korrosion. - : Wiley. - 0947-5117 .- 1521-4176. ; 69:10, s. 1431-1440
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- Isothermal oxidation behavior of NiCr and NiCrAlY coatings deposited onto low alloy 16Mo3 steel by high-velocity air fuel (HVAF) process was investigated in 5% O-2+20% H2O+N-2 at 600 degrees C for 168h. Whereas NiCrAlY showed lower mass gain compared to NiCr, both coatings succeeded in maintaining the integrity with the substrate during the exposure without any breakaway oxidation. A thin Cr-rich oxide scale (Cr2O3) formed on NiCr, and a thin mixed oxide scale (Al2O3 with NiCr2O4) formed on NiCrAlY significantly increasing the oxidation protection in the presence of water vapor.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Korrosionsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Corrosion Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- NiCr
- NiCrAlY
- oxidation protection
- thermal spray coating
- water vapor
- Manufacturing and materials engineering
- Produktions- och materialteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas