Influence of build layout and orientation on microstructural characteristics of electron beam melted Alloy 718

• Effects of build layout and orientation consisting of (a) height from the build plate (Z-axis), (b) distance between samples, and (c) location in the build plate (X-Y plane) on porosity, NbC fraction, and hardness in electron beam melted (EBM) Alloy 718 were studied. The as-built samples predominantly showed columnar structure with strong ˂001˃ crystallographic orientation parallel to the build direction, as well as NbC and ÎŽ-phase in inter-dendrites and grain boundaries. These microstructural characteristics were correlated with the thermal history, specifically cooling rate, resulted from the build layout and orientation parameters. The hardness and NbC fraction of the samples increased around 6% and 116%, respectively, as the height increased from 2 to 45 mm. Moreover, by increasing the height, formation of ÎŽ-phase was also enhanced associated with lower cooling rate in the samples built with a greater distance from the build plate. However, the porosity fraction was unaffected. Increasing the sample gap from 2 to 10 mm did not change the NbC fraction and hardness; however, the porosity fraction increased by 94%. The sample location in the build chamber influenced the porosity fraction, particularly in interior and exterior areas of the build plate. The hardness and NbC fraction were not dependent on the sample location in the build chamber. © 2018, The Author(s).

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

NATURVETENSKAP  -- Kemi -- Analytisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Analytical Chemistry (hsv//eng)

NATURVETENSKAP  -- Geovetenskap och miljövetenskap -- Geokemi (hsv//swe)

NATURAL SCIENCES  -- Earth and Related Environmental Sciences -- Geochemistry (hsv//eng)

Nyckelord

3D printers

Cooling

Electron beam melting

Electron beams

Grain boundaries

Hardness

Location

Niobium compounds

Porosity

Alloy 718

Build direction

Columnar structures

Crystallographic orientations

Micro-structural characteristics

Micro-structural characterization

Orientation parameter

Sample location

Porous plates

Manufacturing and materials engineering

Produktions- och materialteknik

Production Technology

Produktionsteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)