Effect of Different Post-treatments on the Microstructure of EBM-Built Alloy 718
-
- Goel, Sneha, 1993- (författare)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW
-
- Ahlfors, Magnus (författare)
- Quintus Technologies AB, Västerås, Sweden
-
- Bahbou, Fouzi (författare)
- ARCAM AB, Mölndal, Sweden
-
visa fler...
-
- Joshi, Shrikant V., 1960- (författare)
- Högskolan Väst,Forskningsmiljön produktionsteknik(PTW)
-
visa färre...
-
(creator_code:org_t)
- 2018-10-29
- 2019
- Engelska.
-
Ingår i: Journal of materials engineering and performance (Print). - : Springer Science and Business Media LLC. - 1059-9495 .- 1544-1024. ; 28:2, s. 673-680
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://hv.diva-port... (primary) (Raw object)
-
https://link.springe...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Electron beam melting (EBM) of Alloy 718 is of rapidly growing interest as it allows cost-effective production of complex components. However, the inherent flaws in the component in as-built state are of concern in view of the severe working conditions in which Alloy 718 components typically operate. The present work entails an investigation of changes in microstructure that accompany some post-treatments that are being widely considered to address defects in EBM processed Alloy 718. The effect of two different post-treatments, namely hot isostatic pressing (HIP) and a combined HIP + heat treatment (HT) carried out inside the HIP vessel, have been studied and results from as-built and post-treated specimens were compared in terms of porosity/lack-of-fusion, microstructure, phase constitution (NbC content, ÎŽ-phase) and micro-hardness. Post-treatment resulted in reduction in defect content by more than an order of magnitude. HIPing led to complete dissolution of ÎŽ phase. In comparison to as-built material, HIPed specimens exhibited significant drop in hardness. However, a sharp ârecoveryâ of hardness to yield values higher than in as-built condition was observed after HIP + HT and can be attributed to precipitation of γâ²â² phase. © 2018, The Author(s).
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- 3D printers
- Cost effectiveness
- Defects
- Electron beam melting
- Electron beams
- Hardness
- Heat treatment
- Hot isostatic pressing
- Microhardness
- Microstructure
- Alloy 718
- Complete dissolution
- Complex components
- Cost-effective production
- Defect contents
- Phase constitution
- Post treatment
- Yield value
- Niobium compounds
- Manufacturing and materials engineering
- Produktions- och materialteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas