- Artikel/kapitelEngelska2019
Förlag, utgivningsår, omfång ...
-
2018-11-07
-
Informa UK Limited,2019
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:hv-13177
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-13177URI
-
https://doi.org/10.1080/14786435.2018.1540891DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Published online: 07 Nov 2018Funder: Natural Sciences and Engineering Research Council of Canada
-
The dynamic impact response of IN 718 and ATI 718Plus®, in both the solution heat treated and age-hardened conditions, were investigated at different deformation temperatures and strain rates using a direct impact Hopkinson pressure bar. Analyses of the results provide a vital but previously not reported information that the ATI 718Plus® offers a higher resistance to damage during high strain rate ballistic impact deformation compared to the most widely used Iron-nickel based superalloy, Inconel 718. ATI 718Plus® showed higher strain hardening and strain rate sensitivity, in both heat treatment conditions, than IN 718. The difference in the deformation behaviour of both alloys, in the annealed condition, is attributable to the compositional modification in ATI 718Plus® which has been reported to lower its stacking fault energy and increases the tendency for deformation twinning. However, in the age-hardened condition, the difference is believed to be related to the disparity in the operative strengthening mechanism, of the precipitates present in both alloys. Furthermore, a higher susceptibility to strain location and the formation of adiabatic shear band, in aged IN 718, is attributable to the stronger temperature-softening characteristics observed in the alloy and to the limited strain hardening tendency under dynamic impact loading. © 2018, © 2018 Informa UK Limited, trading as Taylor & Francis Group.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Andersson, Joel,1981-Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW(Swepub:hv)joan0056
(författare)
-
Ojo, Olanrewaju A.University of Manitoba, Department of Mechanical Engineering, Winnipeg, Canada (CAN)
(författare)
-
University of Manitoba, Department of Mechanical Engineering, Winnipeg, Canada (CAN)Avdelningen för svetsteknologi (SV)
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Philosophical Magazine: Informa UK Limited99:4, s. 419-4371478-64351478-6443
Internetlänk
Hitta via bibliotek
Till lärosätets databas