Effect of interpass temperature on residual stresses in multipass welds produced using low transformation temperature filler alloy

Appeared or available online: den 10 september 2013
Weld filler alloys that exploit transformation plasticity through low austenite to martensite transformation temperatures offer an effective method of reducing residual stresses in strong steel welds. However, in multipass welds, the heat input from later weld passes may be insufficient to retransform prior welding passes, leading to the accumulation of thermally induced strains and elevated residual stresses. In this work, the residual stress distributions produced around arc welds fabricated with a martensitic weld filler alloy that transforms at a low temperature have been studied as a function of the number of passes deposited and the interpass temperature. It is found that when the interpass temperature is above the transformation temperature of the weld metal, the entire multipass weld transforms as a single entity, thus permitting the optimum exploitation of the transformation plasticity. In contrast, the deposition of new metal with a relatively low interpass temperature leads to increased residual stresses in the underlying layers, reducing or eliminating the beneficial stress states previously created.

Stone, H. J.Unversity of Cambridge (författare)
Karlsson, Leif,1956-Högskolan Väst,Avd för maskinteknik,PTW, Welding technology(Swepub:hv)leikar (författare)
Kelleher, J.ISIS Facility, Rutherford Appleton Laboratory (författare)
Moat, R. J.The Open University (författare)
Kornmeier, J. R.Forschungs-Neutronenquelle Heinz Maier-Leibnitz (författare)
Kemellia, DalaeiESAB AB, Lindholmsalln 9, 417 55 Göteborg (författare)
Bhadeshia, H.K.D.H.University of Cambridge (författare)
University of CambridgeUnversity of Cambridge (creator_code:org_t)

Ingår i:Science and technology of welding and joining19:1, s. 44-511362-17181743-2936

Av författaren/redakt...: Ramjaun, T.; Stone, H. J.; Karlsson, Leif, ...; Kelleher, J.; Moat, R. J.; Kornmeier, J. R.; visa fler...; Kemellia, Dalaei; Bhadeshia, H.K.D ...; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.