- Ramjaun, T. (författare)
- University of Cambridge
-
- Stone, H. J. (författare)
- Unversity of Cambridge
-
- Karlsson, Leif, 1956- (författare)
- Högskolan Väst,Forskningsmiljön produktionsteknik(PTW),PTW, Welding technology
-
visa fler...
-
- Kelleher, J. (författare)
- ISIS Facility, Rutherford Appleton Laboratory
-
- Ooi, S.W. (författare)
- University of Cambridge
-
- Dalaei, K (författare)
- ESAB AB, Lindholmsalln 9, 417 55 Göteborg
-
- Kornmeier, J. R. (författare)
- Forschungs-Neutronenquelle Heinz Maier-Leibnitz
-
- Bhadeshia, H.K.D.H. (författare)
- University of Cambridge
-
visa färre...
-
(creator_code:org_t)
- 2014
- 2014
- Engelska.
-
Ingår i: Science and technology of welding and joining. - 1362-1718 .- 1743-2936. ; 19:6, s. 461-467
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Transformation plasticity can be utilised to control residual stresses in steel welds. This requires special filler alloys that transform at a sufficiently low temperature to compensate for accumulated thermal contraction strains. However, the welding parameters needed to optimise the effect in multipass joints have yet to be established. This topic has been investigated by characterising the residual stress distribution in multipass welds fabricated with different welding alloys and baseplates using neutron diffraction to assess the effects of dilution and baseplate strength. While the use of richly alloyed weld metal does enhance fatigue performance in single pass joints, the extent of stress relief that can be derived from transformation plasticity is reduced due to incomplete martensitic transformation when further layers are deposited. For all cases studied, compressive stresses were measured in the weld metal with balancing tensile stress in the heat affected zone of the plate. The magnitude of the tension was observed to be a function of the strength of the baseplate. Recommendations are also presented for the combination of welding and material parameters that lead to the optimum exploitation of transformation plasticity as a method for boosting the fatigue performance of multipass welded joints.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- Martensitic weld metal; Residual stress; Transformation induced plasticity; Welding phase transformation
- Manufacturing and materials engineering
- Produktions- och materialteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas