Experimental evaluation of normal and shear delamination in cellulose-based materials using a cohesive zone model

Biel, Anders,1977-Karlstad University,Karlstads universitet,Institutionen för ingenjörsvetenskap och fysik (from 2013) (författare)

An experimental study to characterize properties controlling delamination of paperboard is presented. The normal and shear traction-separation laws are measured and evaluated using a double cantilever beam (DCB) and a split double cantilever beam (SCB) specimen. The DCB-experiments provides normal separation data in good agreement with results using alternative experimental techniques. From the measured data, both normal and shear fracture resistance data are obtained. A length parameter is introduced. The length parameter allows for the cohesive law to be obtained from a dimensionless master curve which is valid both for normal and shear loading. Taking advantage of the master curve, a mixed-mode potential is proposed. The mixed-mode potential is implemented as a user interface to a finite element code. As a final test, the experimental setups of the DCB and SCB specimens are simulated to validate the identified normal and shear properties.

TEKNIK OCH TEKNOLOGIER Materialteknik Pappers-, massa- och fiberteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Paper, Pulp and Fiber Technology hsv//eng
TEKNIK OCH TEKNOLOGIER Maskinteknik Teknisk mekanik hsv//swe
ENGINEERING AND TECHNOLOGY Mechanical Engineering Applied Mechanics hsv//eng
Cellulose-based materials
Paperboard
Experiments
traction-separation law
Mixed-mode potential
Materialteknik
Materials Engineering
Cellulose-based materials
Experiments
Mixed-mode potential
Paperboard
traction–separation law

Tryding, JohanLund University,Lunds universitet,Hållfasthetslära,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Solid Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH,Tetra Pak AB(Swepub:lu)soli-jtg (författare)
Ristinmaa, MattiLund University,Lunds universitet,Hållfasthetslära,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,LTH profilområde: Nanovetenskap och halvledarteknologi,LTH profilområden,Solid Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH,LTH Profile Area: Nanoscience and Semiconductor Technology,LTH Profile areas,Faculty of Engineering, LTH(Swepub:lu)hall-mri (författare)
Johansson-Naeslund, MarkusTetra Pak, Lund (författare)
Tuvesson, OscarTetra Pak, Lund (författare)
Stigh, Ulf,1956-Karlstad University,Karlstads universitet,Institutionen för ingenjörsvetenskap och fysik (from 2013)(Swepub:kau)ulfstigh (författare)
Karlstads universitetInstitutionen för ingenjörsvetenskap och fysik (from 2013) (creator_code:org_t)

Ingår i:International Journal of Solids and Structures: Elsevier2520020-76831879-2146

Av författaren/redakt...: Biel, Anders, 19 ...; Tryding, Johan; Ristinmaa, Matti; Johansson-Naeslu ...; Tuvesson, Oscar; Stigh, Ulf, 1956 ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Pappers massa oc ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Maskinteknik; och Teknisk mekanik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.