Improved dispersion of grafted starch granules leads to lower water resistance for starch-g-PLA/PLA composites
-
- Yang, Xi (författare)
- KTH,Fiber- och polymerteknologi
-
- Finne-Wistrand, Anna (författare)
- KTH,Fiber- och polymerteknologi
-
- Hakkarainen, Minna (författare)
- KTH,Polymerteknologi
-
(creator_code:org_t)
- Elsevier, 2013
- 2013
- Engelska.
-
Ingår i: Composites Science And Technology. - : Elsevier. - 0266-3538 .- 1879-1050. ; 86, s. 149-156
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Polylactide (PLA) was grafted on the surface of starch (St) granules to improve the interfacial adhesion between starch granules and PLA matrix in starch/PLA blends. The grafting significantly improved strain at failure values of St-g-PLA/PLA 25:75 blends as compared to starch/PLA 25:75 blends. However, unexpectedly the water resistance of the films significantly deteriorated after the surface grafting. SEM and FTIR analysis showed that St-g-PLA was evenly distributed at the film surface and in the bulk, while unmodified starch was encapsulated inside the PLA matrix. This resulted in rapid leaching of St-g-PLA from the films during aging in water, while the unmodified starch granules were protected by PLA matrix.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Kompositmaterial och -teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Composite Science and Engineering (hsv//eng)
Nyckelord
- Polymer matrix composites (PMCs)
- Environmental degradation
- Mechanical properties
- Infrared (IR) spectroscopy
- Scanning electron microscopy (SEM)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas