Ekelund, MariaKTH,Fiber- och polymerteknologi
(författare)
Long-term performance of poly(vinyl chloride) cables, Part 2 : Migration of plasticizer
- Artikel/kapitelEngelska2008
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2008
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-14089
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-14089URI
-
https://doi.org/10.1016/j.polymdegradstab.2008.05.030DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20100713
-
Cable samples with plasticized poly(vinyl chloride) insulations were aged in air at temperatures between 80 and 155 degrees C. The concentrations of the plasticizer (di-(2-ethylhexyl) phthalate, DEHP) in the insulations of the aged cables were determined by extraction of samples in tetrahydrofuran followed by analysis of the extract by liquid chromatography. The plasticizer concentration data for different ageing times were analysed by numerical methods, fitting Fick's second law with a concentration-dependent diffusivity. The analysis showed that the transport of the plasticizer to the surrounding air phase was controlled by diffusion at 120 and 155 degrees C with an activation energy of 89 kJ mol(-1). The evaporation of the plasticizer from the outer boundary was rate controlling at lower temperatures (<= 100 degrees C), The rate of evaporation was initially constant and independent of the plasticizer concentration at both 80 and 100 degrees C. The activation energy for the initial DEHP loss rate from PVC at these temperatures was the same as that obtained for evaporation of pure DEHP on a glass plate at 60-100 degrees C measured by thermogravimetry, 98 2 kJ mol-1. Furthermore, the evaporation rate of pure DEHP on a glass plate was also of the same order of magnitude as the rate of plasticizer loss from the cable insulation. Extrapolation of the plasticizer loss rate data (from the cable at 80 degrees C and from pure liquid DEHP at temperatures between 60 and 100 IQ to 25 degrees C predicted a maximum loss of plasticizer of 1% over 25 years. This is in accordance with earlier presented data and with the data presented in this report.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Azhdar, BruskaKTH,Fiber- och polymerteknologi(Swepub:kth)u1kombby
(författare)
-
Hedenqvist, Mikael S.KTH,Fiber- och polymerteknologi(Swepub:kth)u10rkaxe
(författare)
-
Gedde, Ulf WKTH,Fiber- och polymerteknologi(Swepub:kth)u1j56evm
(författare)
-
KTHFiber- och polymerteknologi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Polymer degradation and stability: Elsevier BV93:9, s. 1704-17100141-39101873-2321
Internetlänk
Hitta via bibliotek
Till lärosätets databas