A New Class of Materials for Magneto-Optical Applications : Transparent Amorphous Thin Films of Fe-B-Nb and Fe-B-Nb-Y Metallic Glassy Alloys
-
- Masood, Ansar (författare)
- KTH,Materialvetenskap
-
- Tamaki, Takahiko (författare)
- KTH,Materialvetenskap
-
- Ström, Valter (författare)
- KTH,Teknisk materialfysik
-
visa fler...
-
- Borgenstam, Annika (författare)
- KTH,Metallografi
-
- Ågren, John (författare)
- KTH,Metallografi
-
- Rao, K. Venkat (författare)
- KTH,Teknisk materialfysik
-
visa färre...
-
(creator_code:org_t)
- 2014
- 2014
- Engelska.
-
Ingår i: IEEE transactions on magnetics. - 0018-9464 .- 1941-0069. ; 50:4, s. 4004005-
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Optically highly transparent, soft magnetic thin films (4-18 nm thick) of Fe-B-Nb- and Fe-B-Nb-Y-based glassy metal targets were grown on quartz substrates by pulsed laser deposition, and their optical and magneto-optical properties were investigated over the visible spectrum (400-700 nm). All the films found to be fully amorphous in structure were continuous with uniform thickness and surface morphology. Their optical transmittance in the range 50%-85% was found to be film thickness dependent over the entire visible regime. The Verdet constant (V) and Faraday rotation angle (theta(f)) for different films (similar to 4-18 nm) investigated as a function of wavelength (lambda) show considerably higher values for the films of Fe-B-Nb-Y alloy as compared with those for Fe-B-Nb films, e. g., the similar to 4 nm film of Fe-B-Nb-Y alloy exhibits V similar to 49 degrees/Oe cm and theta(f)similar to 26 degrees/mu m while it decreased to similar to 29.4 degrees/Oe and similar to 11.8 degrees/mu m, respectively, for the Fe-B-Nb alloy at lambda=611 nm. A linear relationship is found for the wavelength dependence of V and theta(f) for both alloy systems. To the best of our knowledge, these values are considerably higher than those reported for any other magneto-optic material. The films are found to be soft magnetic with a high saturation moment while their magnetic coercivity values increases with thinness of the films. The observed combination of optical and magneto-optical properties of this new class of amorphous metallic films makes them viable for multifunctional magneto-optical applications.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Amorphous magnetic materials
- Faraday rotation
- pulsed laser deposition (PLD)
- soft magnetic thin films