Iron-Catalyzed Polymerization of Alkoxysulfonate-Functionalized 3,4-Ethylenedioxythiophene Gives Water-Soluble Poly(3,4-ethylenedioxythiophene) of High Conductivity
-
- Karlsson, Roger (författare)
- Linköpings universitet,Organisk Kemi,Tekniska högskolan
-
- Herland, Anna (författare)
- Linköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan
-
- Hamedi, Mahiar (författare)
- Linköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan
-
visa fler...
-
- Wigenius, Jens (författare)
- Linköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan
-
- Åslund, Andreas (författare)
- Linköpings universitet,Organisk Kemi,Tekniska högskolan
-
- Liu, Xianjie (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska högskolan
-
- Fahlman, Mats (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska högskolan
-
- Inganäs, Olle (författare)
- Linköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan
-
- Konradsson, Peter (författare)
- Linköpings universitet,Organisk Kemi,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- 2009-04-14
- 2009
- Engelska.
-
Ingår i: Chemistry of Materials. - : American Chemical Society (ACS). - 0897-4756 .- 1520-5002. ; 21:9, s. 1815-1821
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Chemical polymerization of a 3,4-ethylenedioxythiophene derivative bearing a sulfonate group (EDOTS) is reported. The polymer, PEDOT-S, is fully water-soluble and has been produced by polymerizing EDOT-S in water, using Na2S2O8 and a catalytic amount of FeCl 3. Elemental analysis and XPS measurements indicate that PEDOT-S is a material with a substantial degree of self-doping, but also contains free sulfate ions as charge-balancing counterions of the oxidized polymer. Apart from selfdoping PEDOT-S, the side chains enable full water solubility of the material; DLS studies show an average cluster size of only 2 nm. Importantly, the solvation properties of the PEDOT-S are reflected in spin-coated films, which show a surface roughness of 1.2 nm and good conductivity (12 S/cm) in ambient conditions. The electro-optical properties of this material are shown with cyclic voltammetry and spectroelectrochemical experiment reveals an electrochromic contrast (̃48% at λmax ) 606 nm).
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- Ambient conditions
- Catalytic amounts
- Catalyzed polymerization
- Chemical polymerization
- Cluster sizes
- Counterions
- Electrochromic contrast
- Electrooptical properties
- Elemental analysis
- Ethylenedioxythiophene
- Functionalized
- High conductivity
- Self-doping
- Side chains
- Solvation properties
- Spectroelectrochemical
- Spin-coated films
- Sulfate ion
- Sulfonate groups
- Water solubilities
- XPS measurements
- NATURAL SCIENCES
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas