CdSe quantum dots/molecular cobalt catalyst co-grafted open porous NiO film as a photocathode for visible light driven H-2 evolution from neutral water
-
Meng, Peng (författare)
-
Wang, Mei (författare)
-
Yang, Yong (författare)
-
visa fler...
-
Zhang, Shuai (författare)
-
- Sun, Licheng (författare)
- KTH,Organisk kemi,Dalian Univ Technol, State Key Lab Fine Chem, DUT KTH Joint Educ & Res Ctr Mol Devices, China
-
visa färre...
-
(creator_code:org_t)
- 2015
- 2015
- Engelska.
-
Ingår i: Journal of Materials Chemistry A. - : Royal Society of Chemistry (RSC). - 2050-7488 .- 2050-7496. ; 3:37, s. 18852-18859
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- An active noble-metal-free photocathode was fabricated by co-grafting water-soluble thioglycolic acid-stabilized CdSe quantum dots and a molecular cobaloxime catalyst (CoP) through chemical linkage on a p-type open porous NiO film. This photocathode was used as a working electrode in a three-electrode cell, which displayed a photocurrent density up to 110 mu A cm(-2) at an applied potential of 0 V vs. NHE in 0.1 M Na2SO4 solution at pH 6.8 upon visible light illumination. The comparative studies showed that the open porous NiO/CdSe electrode did display a higher photocurrent density than that exhibited by an analogous planar NiO/CdSe electrode made by doctor-blading a NiO paste. Long-time photoelectrolysis experiments revealed that about 83% of the photocurrent density remained after 3.5 h illumination at 0.2 V vs. NHE. The open porous NiO/CdSe/CoP photocathode showed a considerably better current density and photocatalytic stability compared to the so-far reported dye-or QD-sensitized NiO cathodes with a cobaloxime catalyst chemically attached or physically adsorbed on the electrode surface under similar conditions.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas