In situ study of selective dissolution of duplex stainless steel 2205 by electrochemical scanning tunnelling microscopy
-
Femenia, M. (författare)
-
- Pan, Jinshan (författare)
- KTH,Materialvetenskap
-
- Leygraf, Christofer (författare)
- KTH,Materialvetenskap
-
visa fler...
-
Luukkonen, P. (författare)
-
visa färre...
-
(creator_code:org_t)
- 2001
- 2001
- Engelska.
-
Ingår i: Corrosion Science. - 0010-938X .- 1879-0496. ; 43:10, s. 1939-1951
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Selective dissolution of duplex stainless steel 2205 in acidic chloride solutions was studied in situ by electrochemical scanning tunnelling microscopy (STM). In 0.05 M H2SO4 + 1 M NaCl, no appreciable active dissolution was observed by in situ STM imaging at the corrosion potential (E-corr), but at potentials higher than E-corr + 1000 mV some selective dissolution at the austenite-ferrite boundary region occurred. In 4 M H2SO4 + 1 M HCl, STM images revealed active dissolution of ferrite grains at around E-corr + 50 mV. Dissolution of austenite grains started to occur at around E-corr + 150 mV, exhibiting steps of submicron scale on the edges.
Nyckelord
- duplex stainless steel
- in situ
- local
- electrochemical scanning tunnelling microscopy
- selective dissolution
- single-crystal surfaces
- tunneling-microscopy
- pitting corrosion
- localized corrosion
- spectroscopy
- electrodes
- nitrogen
- xps