Effect of conditioning history on the characterization of hardness of thermo-mechanical densified and heat treated poplar wood

• Poplar wood was modified by a combination of thermo-mechanical densification (TMD) and heat treatment (HT) process at five temperatures ranging from 170 to 210°C. A new two-step conditioning method (CM) is suggested, in the course of which the modified wood is submitted to 50°C/99% RH→25°C/65% RH, where RH means relative humidity in the climate chamber. The traditional one-step CM (25°C/65% RH) served as reference. The effects of conditioning history on hardness were observed and analyzed along with the change of dimensional stability. The hardness of the modified wood was lower in the case of the proposed CM due to more set-recovery release, but the extent of that decreased with the HT temperature. For a good hardness, HT200°C should be selected with the proposed CM, which is different from the optimization output of 180°C obtained from the traditional CM. In conclusion, a specific assessment method for the performance characterization of this type of modified wood would be beneficial for the combined TMD and HT processes.

Ämnesord

LANTBRUKSVETENSKAPER  -- Lantbruksvetenskap, skogsbruk och fiske -- Trävetenskap (hsv//swe)

AGRICULTURAL SCIENCES  -- Agriculture, Forestry and Fisheries -- Wood Science (hsv//eng)

Nyckelord

conditioning history

hardness

heat treatment

poplar wood

set-recovery

thermo-mechanical densification

two-step conditioning

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)