Intermediate temperature fuel cells based on doped ceria-LiCl-SrCl2 composite electrolyte
- Artikel/kapitelEngelska2002
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-21280
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-21280URI
-
https://doi.org/10.1016/S0378-7753(01)00874-6DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20100525
-
A new type of oxide-salt composite electrolyte, gadolinium-doped ceria (GDC)-LiCl-SrCl2, was developed and demonstrated its promising use for intermediate temperature (400-700 degreesC) fuel cells (ITFCs). The dc electrical conductivity of this composite electrolyte (0.09-0.13 S cm(-1) at 500-650 degreesC) was 3-10 times higher than that of the pure GDC electrolyte, indicating remarkable proton or oxygen ion conduction existing in the LiCl-SrCl2 chloride salts or at the interface between GDC and the chloride salts. Using this composite electrolyte, peak power densities of 260 and 510 mW cm(-2), with current densities of 650 and 1250 mA cm(-2) were achieved at 550 and 625 degreesC, respectively. This makes the new material a good candidate electrolyte for future low-cost ITFCs.
Ämnesord och genrebeteckningar
-
GDC-LiCl-SrCl2
-
composite electrolyte
-
intermediate temperature fuel cells
-
electrical conductivity
-
solid electrolytes
-
conduction
-
proton
-
operation
-
li2so4
-
nacl
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Zha, S. W.
(författare)
-
Zhang, W.
(författare)
-
Peng, D. K.
(författare)
-
Meng, G. Y.
(författare)
-
Zhu, BinKTH,Kemiteknik(Swepub:kth)u1ybbo7e
(författare)
-
KTHKemiteknik
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Journal of Power Sources104:1, s. 73-780378-77531873-2755
Internetlänk
Hitta via bibliotek
Till lärosätets databas