High-performance epitaxial Na0.5K0.5NbO3 thin films by magnetron sputtering
-
- Blomqvist, Mats (författare)
- KTH,Mikroelektronik och informationsteknik, IMIT,Department of Condensed Matter Physics, Royal Institute of Technology, Stockholm, Sweden
-
- Koh, Jung-Hyuk (författare)
- KTH,Mikroelektronik och informationsteknik, IMIT,Department of Condensed Matter Physics, Royal Institute of Technology, Stockholm, Sweden
-
- Khartsev, Sergiy (författare)
- KTH,Mikroelektronik och informationsteknik, IMIT,Department of Condensed Matter Physics, Royal Institute of Technology, Stockholm, Sweden
-
visa fler...
-
- Grishin, Alexander M. (författare)
- KTH,Mikroelektronik och informationsteknik, IMIT
-
- Andréasson, Johanna (författare)
- Luleå tekniska universitet
-
- Grishin, Alex (författare)
- Department of Condensed Matter Physics, Royal Institute of Technology, Stockholm, Sweden
-
visa färre...
-
(creator_code:org_t)
- AIP Publishing, 2002
- 2002
- Engelska.
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 81:2, s. 337-339
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Epitaxial Na0.5K0.5NbO3 (NKN) thin films have been grown on LaAlO3 substrates by rf magnetron sputtering of a stoichiometric, high-density, ceramic target. X-ray diffraction analysis showed c-axis oriented cube-on-cube growth. Micrometer size interdigital capacitor (IDC) structures were defined on the surface of the NKN film using photolithography. The electrical characterization at 1 MHz showed dissipation factor tan delta of 0.010, tunability 16.5% at 200 kV/cm and dielectric permittivity epsilon(r)=470. The frequency dispersion of epsilon(r) between 1 kHz and 1 MHz was 8.5% and the IDCs showed very good insulating properties with leakage current density on the order of 30 nA/cm(2) at 400 kV/cm. The polarization loop exhibits weak ferroelectric hysteresis with maximum polarization 23.5 muC/cm(2) at 600 kV/cm. These results are promising for tunable microwave devices based on rf sputtered NKN thin films.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- interdigital capacitors
- Functional materials
- Funktionella material
- Engineering Materials