Experimental and modelling study of the effect of tempering on the susceptibility to environment-assisted cracking of AISI 420 martensitic stainless steel
-
- Anantha, Krishnan Hariramabadran (författare)
- KTH,Yt- och korrosionsvetenskap
-
- Örnek, Cem (författare)
- KTH,Yt- och korrosionsvetenskap
-
- Ejnermark, Sebastian (författare)
- Uddeholms AB, Res & Dev, SE-68385 Hagfors, Sweden.
-
visa fler...
-
- Thuvander, Anders (författare)
- Uddeholms AB, Res & Dev, SE-68385 Hagfors, Sweden.
-
- Medvedeva, Anna (författare)
- Uddeholms AB, Res & Dev, SE-68385 Hagfors, Sweden.
-
- Sjostrom, Johnny (författare)
- Uddeholms AB, Res & Dev, SE-68385 Hagfors, Sweden.
-
- Pan, Jinshan, 1962- (författare)
- KTH,Yt- och korrosionsvetenskap
-
visa färre...
-
(creator_code:org_t)
- PERGAMON-ELSEVIER SCIENCE LTD, 2019
- 2019
- Engelska.
-
Ingår i: Corrosion Science. - : PERGAMON-ELSEVIER SCIENCE LTD. - 0010-938X .- 1879-0496. ; 148, s. 83-93
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The resistance to environment-assisted cracking (EAC) of AISI 420 martensitic stainless steel (MSS) was investigated in 0.3 M NaCl solution (room temperature) at constant loads for 30 days. The steel tempered at 250 degrees C was superior to the 500 degrees C-temper, which showed corrosion pits favouring cracking. The fracture surface showed faceted grains, cleavage, striations, and inter- and transgranular cracks, suggesting a mixed stress corrosion cracking (SCC) and hydrogen embrittlement (HE) mechanism as the cause for EAC. Finite element modelling (FEM) indicated strain/stress localization at the mouth of deep pits and at the wall of shallow pits, displaying the favoured locations for pit-to-crack transition.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Korrosionsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Corrosion Engineering (hsv//eng)
Nyckelord
- Martensitic stainless steel
- Residual stress
- Tempering
- Environment-assisted cracking
- Pit-to-crack transition