Abstract
Ämnesord
Stäng
- The ferritic ductile cast iron, SiMo51, with graphite nodules and grain boundary carbides, was tested at 700°C with respect to creep, uniaxial strain and oxidation, investigating the internal damage evolution. Creep curves, with total lives of 65–339 days, show a short primary creep followed by predominantly tertiary creep displaying two stages. The first was associated with cavitation around carbides and nodules with a short initial effect from oxidation. The second was associated with the formation of cracks through linking of elongated voids. Misorientation maps demonstrate local dislocation activity during creep and tensile testing. Oxidation tests, between 15 min and 2 weeks, show that three oxide layers are formed and that an innermost precipitation zone of SiO2 is present in the initial stage. Elemental line scans, compared with thermodynamic calculations, suggest the layers are FeO with precipitates of SiO2 and/or Fe2SiO4, FeO without precipitates, and Fe2O3.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Creep
- ductile cast iron
- EBSD
- oxidation
- tensile test
- Carbides
- Creep testing
- Ferrite
- Grain boundaries
- Hematite
- Internal oxidation
- Molybdenum compounds
- Silica
- Silicon
- Tensile testing
- Dislocation activity
- Ductile cast irons
- Grain boundary carbides
- Internal damages
- Oxidation damage
- Thermodynamic calculations
- Uni-axial strains
- Cast iron
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas