Polyol synthesis of...
Polyol synthesis of (polyvinylpyrrolidone) PVP-Mn3O4 nanocomposite
- Artikel/kapitelEngelska2010
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2010
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-29463
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-29463URI
-
https://doi.org/10.1016/j.jallcom.2010.04.143DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20110208
-
We report on the synthesis of (polyvinylpyrrolidone) PVP-Mn3O4 nanocomposite via a polyol route. Crystalline phase was identified as Mn3O4 and the crystallite size was obtained as 6 +/- 1 nm from X-ray line profile fitting. Average particle size of 6.1 +/- 0.1 nm obtained from TEM analysis reveals nearly single crystalline nature of these nanoparticles in the composite. The capping of PVP around Mn3O4 nanoparticles was confirmed by FT-IR spectroscopy, the interaction being via bridging oxygens of the carbonyl (C=O) and the nanoparticle surface. T-C and T-B for PVP-Mn3O4 nanocomposite were observed at 42K and 28.5 K, respectively. The sample has hysteresis with small coercivity and remanent magnetization at 40K, resembling the superparamagnetic state. ac conductivity measurements on PVP-Mn3O4 nanocomposite revealed a conductivity in the order of 10(-7) S cm(-1) at lower frequencies. The conductivity change with respect to frequency can be explained by electronic exchange occurring between Mr(+2) and Mn+3 existing in sublattice of spinel lattice.
Ämnesord och genrebeteckningar
-
Nanocomposite
-
Nanomagnetic materials
-
ac conductivity
-
Magnetization
-
TECHNOLOGY
-
TEKNIKVETENSKAP
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Bitrak, N.
(författare)
-
Ünal, B.
(författare)
-
Kavas, H.
(författare)
-
Durmus, Z.
(författare)
-
Özden, S.
(författare)
-
Toprak, Muhammet S.KTH,Funktionella material, FNM(Swepub:kth)u1u3m5a2
(författare)
-
KTHFunktionella material, FNM
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Journal of Alloys and Compounds: Elsevier BV502:1, s. 199-2050925-83881873-4669
Internetlänk
Hitta via bibliotek
Till lärosätets databas