Corrosion mechanism of CuAl-NiC abradable seal coating system—The influence of porosity, multiphase, and multilayer structure on the corrosion failure

QC 20220215
In this study, the corrosion behavior of the CuAl-NiC abradable seal coating system in chloride solution was investigated to systematically research the effect of porosity, multiphase, and multilayer structure on the corrosion failure. Through the composition and structure analysis, the corrosion process of the system was predicted and then verified with mercury intrusion porosimetry, cross-section SEM/EDS analysis, and electrochemical measurements. The results demonstrated that the interphase selective corrosion caused the porosity of the top layer to decrease first and then increase during the corrosion development. The interlayer galvanic corrosion, determined by the pore connectivity, is crucial for corrosion failure.

TEKNIK OCH TEKNOLOGIER Materialteknik Annan materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Other Materials Engineering hsv//eng
TEKNIK OCH TEKNOLOGIER Materialteknik Metallurgi och metalliska material hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Metallurgy and Metallic Materials hsv//eng
TEKNIK OCH TEKNOLOGIER Materialteknik Bearbetnings-, yt- och fogningsteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Manufacturing, Surface and Joining Technology hsv//eng
Abradable seal coating system
Galvanic corrosion
Multilayer
Porosity
Aluminum compounds
Chlorine compounds
Coatings
Copper compounds
Corrosive effects
Dealloying
Multilayers
Nickel compounds
Seals
Chloride solutions
Corrosion behavior
Corrosion mechanisms
Electrochemical measurements
Mercury intrusion porosimetry
Multilayer structures
Selective corrosion
Structure analysis
Failure (mechanical)

Zhang, F. (författare)
Njoku, D. I. (författare)
Yu, Y. (författare)
Pan, Jinshan,1962-KTH,Yt- och korrosionsvetenskap(Swepub:kth)u17ks6cf (författare)
Meng, M. (författare)
Li, Y. (författare)
KTHYt- och korrosionsvetenskap (creator_code:org_t)

Ingår i:Journal of Materials Science & Technology: Elsevier BV88, s. 258-2691005-0302

Av författaren/redakt...: Ni, Y.; Zhang, F.; Njoku, D. I.; Yu, Y.; Pan, Jinshan, 19 ...; Meng, M.; visa fler...; Li, Y.; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.