Brittle fracture initiation in decommissioned boiling water reactor pressure vessel head weld

• The brittle fracture initiation behavior and fracture toughness in the ductile-to-brittle transition region for a thermally-aged weld metal of a decommissioned reactor pressure vessel head (in operation at 288 degrees C for 23 effective full power years) and in the non-aged reference condition were investigated. The results show that brittle fracture initiated primarily from non-metallic inclusions. The correlation between frac-ture toughness and brittle fracture initiation type (inclusion debonding or breakage), initiator size, initi-ation location (as-welded or re-heated regions in the weld metal) were analysed. Despite that thermal ageing does not affect significantly the fracture toughness, it could promote the debonding as a brit-tle fracture primary initiation type. The influence of debonded inclusion on the evolution of cumulative damage and brittle fracture initiation was assessed using crystal plasticity modelling.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Brittle fracture

Initiation

Reactor pressure vessel

Weld metal

Inclusion

Toughness